LCP VECTRA® S471-BK010P CELANESE USA
98
- Unit Price:
- $6222 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Glass fiber reinforced
- Application Areas:Home appliance components Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 0.50 | % |
| 流量 | ISO 294-4 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break | ISO 527-2/1A/5 | 120 | Mpa |
| Tensile strain | Break | ISO 527-2/1A/5 | 1.4 | % |
| Tensile modulus | ISO 527-2/1A | 12000 | Mpa | |
| Bending modulus | 23°C | ISO 178 | 12000 | Mpa |
| Bending stress | 23°C | ISO 178 | 185 | Mpa |
| Fracture bending strain | ISO 178 | 2.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 8.0E-6 | cm/cm/°C |
| Across Flow | ISO 11359-2 | 1.7E-5 | cm/cm/°C | |
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 315 | °C |
| 8.0 MPa, Unannealed | ISO 75-2/C | 271 | °C | |
| Melting temperature 3 | ISO 11357-3 | 350 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 1.0E+11 | ohms | |
| Volume resistivity | IEC 60093 | 1.0E+16 | ohms·cm | |
| Relative permittivity | 1 MHz | IEC 60250 | 4.00 | |
| Leakage Trace Index | IEC 60112 | 200 200 (200) | V | |
| Dissipation factor | 1 MHz | IEC 60250 | 7.0E-3 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Injection speed | 中等 | |||
| drying temperature | 150 到 170 | °C | ||
| Processing (melt) temperature | 360 到 375 | °C | ||
| Mold temperature | 80 到 120 | °C | ||
| drying time | 6.0 | hr | ||
| Temperature at the rear of the barrel | 330 到 350 | °C | ||
| Temperature in the middle of the barrel | 340 到 360 | °C | ||
| Temperature at the front of the material cylinder | 345 到 365 | °C | ||
| Spray nozzle temperature | 355 到 370 | °C | ||
| Back pressure | < 3.00 | Mpa | ||
| Hopper temperature | 20 到 40 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 10 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.