Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.2 | % |
| Shrinkage rate | MD:3.00mm4 | 内部方法 | 0.50 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.070 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | Yield,23°C | ISO527-2 | 110 | Mpa |
| Tensile strain | Break,23°C | ISO527-2 | 2.5 | % |
| Tensile modulus | 23°C | ISO527-2 | 6900 | Mpa |
| Bending modulus | 23°C | ISO178 | 6500 | Mpa |
| Friction coefficient vs. Metal5 | | SuzukiMethod | 0.15 | |
| Bending stress | 23°C | ISO178 | 170 | Mpa |
| Friction coefficient 4 | | | 0.20 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 205 | °C |
| Linear coefficient of thermal expansion | MD：-30to100°C | ISO11359-2 | 5.3E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | IEC60093 | 5.6E+16 | ohms·cm |
| Dielectric strength | | IEC60243-1 | 14 | KV/mm |
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| Dissipation factor 6 | 23°C,50Hz | IEC60250 | 2E-03 | |
| Dissipation factor 6 | 23°C,1MHz | IEC60250 | 0.020 | |
| Arc resistance 7 | | IEC60950 | 135 | sec |
| Dielectric constant 5 | 23°C,50Hz | IEC60250 | 3.60 | |
| Dielectric constant 5 | 23°C,1kHz | IEC60250 | 3.80 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 35 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Sale,23°C | ISO2039-2 | 85 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.8mm | UL94 | V-0 | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| BarFlowLength8 | 250°C,1.00mm | 内部方法 | 140 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.