PC LNP™ THERMOCOMP™ DF-1006 BK82025 SABIC INNOVATIVE US
70
- Unit Price:
- $2700 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low extract Easy to form Easy to demould
- Application Areas:Electronic display Medical and nursing suppl
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 24 hr, 50% RH | ASTM D570 | 0.070 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.070 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTM D638 | 8630 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 2.7 | % |
| Break 3 | ASTM D638 | 3.2 | % | |
| Break | ISO 527-2/5 | 7.5 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 8230 | Mpa |
| -- 5 | ISO 178 | 7860 | Mpa | |
| bending strength | Break, 50.0 mm Span | ASTM D790 | 149 | Mpa |
| Tensile strength | Break 3 | ASTM D638 | 114 | Mpa |
| Break | ISO 527-2/5 | 114 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 144 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | ISO 75-2/Bf | 146 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 140 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 6 | ISO 75-2/Af | 142 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 4.0 | hr | ||
| Temperature at the rear of the barrel | 295 到 305 | °C | ||
| Temperature in the middle of the barrel | 310 到 320 | °C | ||
| Temperature at the front of the material cylinder | 320 到 330 | °C | ||
| Back pressure | 0.200 到 0.300 | Mpa | ||
| Screw speed | 30 到 60 | rpm | ||
| drying temperature | 120 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 305 到 325 | °C | ||
| Mold temperature | 80 到 110 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 910 | J/m |
| 23°C 6 | ISO 180/1U | 58 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.