PBT LNP™ LUBRICOMP™ WFL-4034 SABIC INNOVATIVE US
124
- Unit Price:
- $8073 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Aging resistance Filler: Glass fiber reinf 20% filler by weight
- Application Areas:Electrical field Automotive components
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD：24hr | ASTMD955 | 1.0to3.0 | % |
| MD：24hr | ASTMD955 | 0.30to0.50 | % | |
| Water absorption rate | 24hr,50%RH | ASTMD570 | 0.054 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.072 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO527-2/5 | 114 | Mpa |
| Break | ISO527-2/5 | 114 | Mpa | |
| Tensile strain | Yield | ISO527-2/5 | 2.6 | % |
| Break | ISO527-2/5 | 2.6 | % | |
| Elongation rate 3 | Yield | ASTMD638 | 2.6 | % |
| Wear factor | Washer | ASTMD3702Modified | 44.5 | 10^-10in^5-min/ft-lb-hr |
| Ring | ASTMD3702Modified | -0.0200to-0.0100 | 10^-10in^5-min/ft-lb-hr | |
| Tensile modulus 2 | ASTMD638 | 8270 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 118 | Mpa |
| Yield | ASTMD638 | 118 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 7480 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 173 | Mpa |
| Tensile modulus | ISO527-2/1 | 7890 | Mpa | |
| friction coefficient | Static | ASTMD3702Modified | 0.22 | |
| Dynamic | ASTMD3702Modified | 0.24 | ||
| Elongation rate 4 | Break | ASTMD638 | 2.6 | % |
| Bending modulus 5 | ISO178 | 7070 | Mpa | |
| Bending strength 5 | Break,50.0mmSpan | ASTMD790 | 173 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 210 | °C |
| 0.45MPa,Unannealed,3.20mm | ASTMD648 | 222 | °C | |
| Hot deformation temperature 7 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 208 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 222 | °C | |
| Linear coefficient of thermal expansion | TD：-30to30°C | ASTMD696 | 8.9E-05 | cm/cm/°C |
| MD：-30to30°C | ASTMD696 | 3.6E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 7.50 | J |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 2.90 | J | |
| Unscented Izod Impact Strength 5 | 23°C | ISO180/1U | 41 | kJ/m² |
| Suspended wall beam notch impact strength 6 | 23°C | ISO180/1A | 7.8 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.