Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan Flame retardant Thermal stability Filler: Glass mineral 65% filler by weight
Application Areas:Automotive components Sports equipment Pump parts Industrial components Industrial applications Parts under the hood of a Application in the automo Shell
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD	ASTMD955	0.30	%
Shrinkage rate	Shrinkage rate	TD	ASTMD955	0.50	%
Water absorption rate	24hr	ASTMD570	0.10	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Break,23°C	ISO527-2	138	Mpa
	Tensile stress	Break,24°C	ISO527-2	91.7	Mpa
		Tensile stress	Break,150°C	ISO527-2	46.2	Mpa
		Tensile stress	Tensile stress	Break,175°C	ISO527-2	32.4	Mpa
Tensile strain	Break,23°C	ISO527-2	1.0	%
	Tensile strain	Break,24°C	ISO527-2	1.3	%
		Tensile strain	Break,150°C	ISO527-2	2.4	%
		Tensile strain	Tensile strain	Break,175°C	ISO527-2	1.8	%
Bending stress	23°C	ISO178	211	Mpa
	Bending stress	100°C	ISO178	163	Mpa
		Bending stress	150°C	ISO178	69.6	Mpa
		Bending stress	Bending stress	175°C	ISO178	55.8	Mpa
Tensile modulus		ASTMD638	20700	Mpa
	Tensile modulus	23°C	ISO527-2	19700	Mpa
		Tensile modulus	100°C	ISO527-2	15400	Mpa
			Tensile modulus	150°C	ISO527-2	5720	Mpa
			Tensile modulus	Tensile modulus	175°C	ISO527-2	5100	Mpa
elongation	Break	ASTMD638	1.2	%
Bending modulus		ASTMD790	17900	Mpa
	Bending modulus	23°C	ISO178	9100	Mpa
		Bending modulus	100°C	ISO178	6830	Mpa
			Bending modulus	150°C	ISO178	2480	Mpa
			Bending modulus	Bending modulus	175°C	ISO178	2280	Mpa
bending strength		ASTMD790	210	Mpa
Tensile strength		ASTMD638	131	Mpa
shear strength		ASTMD732	71.0	Mpa
CompressiveLength	13.0mm	ASTMD695	189	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	271	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	271	°C
Peak melting temperature		ASTMD3418	311	°C
Linear coefficient of thermal expansion	MD：0to100°C	ASTME831	2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：100to200°C	ASTME831	1.7E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：0to100°C	ASTME831	3.7E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	8.1E-05	cm/cm/°C
Melting temperature		ISO11357-3	311	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Arc resistance		ASTMD495	125	sec
Volume resistivity		ASTMD257	4E+14	ohms·cm
Compared to the anti leakage trace index	CTI	UL746	600	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Unscented Izod impact strength	23°C	ISO180/1U	32	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO179/1eU	44	kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.