PPA AMODEL® AFA-6133 BK324 SOLVAY USA

138

Unit Price:
$4047 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
42.7MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Filler: Glass fiber reinf 33% filler by weight
Application Areas:Connector Vehicle electronics Application in the automo Spool
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD	ASTMD955	0.30	%
Shrinkage rate	Shrinkage rate	TD	ASTMD955	0.60	%
Water absorption rate	24hr	ASTMD570	0.20	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ASTMD638	16100	Mpa
	Tensile modulus	23°C	ISO527-2	14500	Mpa
		Tensile modulus	100°C	ISO527-2	9170	Mpa
			Tensile modulus	150°C	ISO527-2	5930	Mpa
			Tensile modulus	Tensile modulus	175°C	ISO527-2	5100	Mpa
Tensile strength		ASTMD638	199	Mpa
Tensile stress	Yield,23°C	ISO527-2	186	Mpa
	Tensile stress	Yield,100°C	ISO527-2	114	Mpa
		Tensile stress	Yield,150°C	ISO527-2	75.2	Mpa
		Tensile stress	Tensile stress	Yield,175°C	ISO527-2	63.4	Mpa
elongation	Break	ASTMD638	1.7	%
Tensile strain	Break,23°C	ISO527-2	1.6	%
	Tensile strain	Break,24°C	ISO527-2	2.4	%
		Tensile strain	Break,150°C	ISO527-2	5.1	%
		Tensile strain	Tensile strain	Break,175°C	ISO527-2	4.9	%
Bending modulus		ASTMD790	13100	Mpa
	Bending modulus	23°C	ISO178	12600	Mpa
		Bending modulus	100°C	ISO178	8070	Mpa
			Bending modulus	150°C	ISO178	4960	Mpa
			Bending modulus	Bending modulus	175°C	ISO178	4620	Mpa
bending strength		ASTMD790	224	Mpa
Bending stress	23°C	ISO178	259	Mpa
	Bending stress	100°C	ISO178	161	Mpa
		Bending stress	150°C	ISO178	101	Mpa
		Bending stress	Bending stress	175°C	ISO178	87.6	Mpa
compressive strength		ASTMD695	145	Mpa
shear strength		ASTMD732	80.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/Af	282	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ASTMD648	277	°C
Peak melting temperature		ASTMD3418	310	°C
Melting temperature		ISO11357-3	310	°C
Linear coefficient of thermal expansion	MD：0to100°C	ASTME831	1.7E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：100to200°C	ASTME831	7E-06	cm/cm/°C
		Linear coefficient of thermal expansion	TD：0to100°C	ASTME831	6.4E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	1.1E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		ASTMD257	1E+15	ohms
Volume resistivity		ASTMD257	1E+15	ohms·cm
Dielectric strength	3.17mm	ASTMD149	24	KV/mm
Dielectric constant	100Hz	ASTMD150	4.40
Dielectric constant	Dielectric constant	1MHz	ASTMD150	4.10
Dissipation factor	1MHz	ASTMD150	0.011
Compared to the anti leakage trace index	CTI	UL746	PLC1
High arc combustion index (HAI)	0.75mm	UL746	PLC0
	High arc combustion index (HAI)	1.5mm	UL746	PLC0
	High arc combustion index (HAI)	High arc combustion index (HAI)	3.0mm	UL746	PLC0
Hot wire ignition (HWI)	0.75mm	UL746	PLC0
	Hot wire ignition (HWI)	1.5mm	UL746	PLC0
	Hot wire ignition (HWI)	Hot wire ignition (HWI)	3.0mm	UL746	PLC0

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179/1eU	46	kJ/m²
Unscented Izod impact strength	23°C	ISO180/1U	44	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
FlameRating3	0.8mm	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.