PPA AMODEL® AT-1116HS SOLVAY USA
115
- Unit Price:
- $10295 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 16% filler by weight High temperature resistan
- Application Areas:Electrical applications Industrial components Industrial applications Machine/mechanical compon Metal substitution Connector Parts under the hood of a Vehicle electronics Application in the automo currency Spool bearing
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | ASTMD955 | 0.60 | % |
| TD | ASTMD955 | 0.60 | % | |
| Water absorption rate | 24hr | ASTMD570 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break,23°C | ISO527-2 | 160 | Mpa |
| Break,24°C | ISO527-2 | 65.5 | Mpa | |
| Tensile strain | Break,23°C | ISO527-2 | 3.7 | % |
| Break,24°C | ISO527-2 | 4.2 | % | |
| Tensile modulus | ASTMD638 | 6480 | Mpa | |
| 23°C | ISO527-2 | 6890 | Mpa | |
| 100°C | ISO527-2 | 6690 | Mpa | |
| elongation | Break | ASTMD638 | 3.8 | % |
| Bending modulus | ASTMD790 | 6000 | Mpa | |
| 23°C | ISO178 | 6690 | Mpa | |
| 100°C | ISO178 | 4960 | Mpa | |
| bending strength | ASTMD790 | 226 | Mpa | |
| Bending stress | 23°C | ISO178 | 197 | Mpa |
| 100°C | ISO178 | 141 | Mpa | |
| compressive strength | ASTMD695 | 124 | Mpa | |
| shear strength | ASTMD732 | 69.6 | Mpa | |
| Tensile strength | ASTMD638 | 161 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Peak melting temperature | ASTMD3418 | 310 | °C | |
| Linear coefficient of thermal expansion | MD：0to100°C | ASTME831 | 2.2E-05 | cm/cm/°C |
| MD：100to200°C | ASTME831 | 1.6E-05 | cm/cm/°C | |
| TD：0to100°C | ASTME831 | 7.5E-05 | cm/cm/°C | |
| TD：100to200°C | ASTME831 | 1.2E-04 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Annealed | ASTMD648 | 268 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 258 | °C | |
| 1.8MPa,Annealed | ASTMD648 | 254 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 86 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO180/1U | 53 | kJ/m² |
| Dart impact equipped with measuring instruments | EnergyatMaxumumLoad2 | ASTMD3763 | 1.76 | J |
| EnergyatMaxumumLoad3 | ASTMD3763 | -- | J | |
| TotalEnergy | ASTMD3763 | 10.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.