PPA AMODEL® AS-4133 SOLVAY USA
207
- Unit Price:
- $5728 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 123MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance high strength High temperature resistan Filler: Glass fiber reinf 33% filler by weight
- Application Areas:Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Balance, 23 ℃, 50% RH | % | 0.21到1.2 | ||
| 23℃ | g/cm³ | 1.29到1.78 | ||
| % | 0.14到1.0 | |||
| 23℃,24hr | % | 0.30到0.51 | ||
| % | 0.12到0.30 | |||
| Lateral flow: 23 ℃ | mm/mm | 119.4E-3到0.254 | ||
| Flow: 23 ℃ | mm/mm | 48.3E-3到129.5E-3 | ||
| -- | 1.33到1.73 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| compressive strength | 23℃ | MPa | 142.76到196.55 | |
| shear strength | 23℃ | MPa | 88.28到107.59 | |
| Poisson's ratio | 23℃ | 0.41 | ||
| Tensile modulus | 摩擦系数 | 0.15到0.52 | ||
| 23℃ | MPa | 5337.93到17586.21 | ||
| MPa | 5200.0到18344.83 | |||
| MPa | 88.28到260.0 | |||
| MPa | 8827.59到14482.76 | |||
| MPa | 137.93到392.41 | |||
| MPa | 5137.93到18620.69 | |||
| MPa | 126.21到364.14 | |||
| Fracture, 23 ℃ | % | 1.5到3.1 | ||
| % | 1.0到2.5 | |||
| MPa | 131.72到400.0 | |||
| MPa | 108.28到262.76 | |||
| MPa | 162.76到199.31 | |||
| Yield, 23 ℃ | % | 1.5到2.6 | ||
| MPa | 102.76到362.76 | |||
| MPa | 12.62到270.34 | |||
| % | 1.4到2.5 | |||
| MPa | 68.97到250.34 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | °C | 258到313 | ||
| RTIElec | °C | 140到150 | ||
| Evolution Calendar intelligent importer | °C | 118到150 | ||
| 0.45MPa, unannealed | °C | 275到308 | ||
| °C | 273到312 | |||
| 1.8MPa, unannealed | °C | 249到304 | ||
| °C | 247到292 | |||
| Continuous use temperature | °C | 140到186 | ||
| 8.0Mpa, unannealed | °C | 165到230 | ||
| transverse | mm/mm/°C | 68.6E-5到127.0E-5 | ||
| mm/mm/°C | 63.5E-5到177.8E-5 | |||
| flow | mm/mm/°C | 38.1E-5到50.8E-5 | ||
| mm/mm/°C | 185.4E-5到25.4E-5 | |||
| mm/mm/°C | 195.6E-5到25.4E-5 | |||
| 0.45MPa, annealed | °C | 296到320 | ||
| 1.8MPa, annealed | °C | 283到300 | ||
| RTI | °C | 119到150 | ||
| -- | °C | 310到312 | ||
| °C | 299到315 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| -- | ohms | 1.0E+2到2.5E+15 | ||
| ohms | 1.0E+5到2.5E+16 | |||
| 23℃ | V/mil | 450到590 | ||
| 3.66 | ||||
| ohms·cm | 1.0E+3到2.5E+15 | |||
| V/mil | 420到1100 | |||
| ohms·cm | 1.0E+15到2.6E+16 | |||
| 4.9E-3到0.015 | ||||
| 3.66到5.52 | ||||
| 4.0E-3到0.017 | ||||
| Compared to the anti leakage trace index | CTI | V | 548到600 | |
| Leakage Trace Index | V | 593到600 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 4.178到19.964 | |
| 23℃ | J | 0.78到2.04 | ||
| kJ/m² | 0.556到3.158 | |||
| kJ/m² | 4.365到15.786 | |||
| J/m | 0.066到0.351 | |||
| N.m | 138.05到788.50 | |||
| J/m | 0.008到0.042 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | 23℃ | 125 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | °C | 743到960 | ||
| Extreme Oxygen Index | % | 23到25 | ||
| Hot filament ignition temperature | °C | 721到926 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.