PC INFINO® SC-1060U Samsung Cheil South Korea
96
- Unit Price:
- $3649 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent High temperature resistan
- Application Areas:Medical packaging
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 流量 : 2.00 mm | ISO 294-4 | 0.50 到 0.70 | % |
| Across Flow : 2.00 mm | ISO 294-4 | 0.50 到 0.70 | % | |
| Across Flow : 3.20 mm | ASTM D955 | 0.50 到 0.70 | % | |
| Flow : 3.20 mm | ASTM D955 | 0.50 到 0.70 | % | |
| Melt flow rate | 300°C/1.2 kg | ASTM D1238, ISO 1133 | 6.0 | g/10 min |
| Density/specific gravity | 本色 | ASTM D792, ISO 1183 | 1.20 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- | ISO 527-2/50 | 2300 | Mpa |
| -- 3 | ASTM D638 | 2300 | Mpa | |
| elongation | Break | ISO 527-2/50 | 110 | % |
| Break 3 | ASTM D638 | 110 | % | |
| Bending modulus | -- 5 | ISO 178 | 2300 | Mpa |
| -- 4 | ASTM D790 | 2300 | Mpa | |
| bending strength | -- 5 | ISO 178 | 93.0 | Mpa |
| -- 4 | ASTM D790 | 91.0 | Mpa | |
| Tensile strength | Break | ISO 527-2/50 | 66.0 | Mpa |
| Break 3 | ASTM D638 | 65.0 | Mpa | |
| Yield | ISO 527-2/50 | 66.0 | Mpa | |
| Yield 3 | ASTM D638 | 65.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | ISO 306/B50 | 147 | °C | |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 138 | °C |
| 0.45 MPa, Unannealed, 4.00 mm | ISO 75-2/B | 138 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 128 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | ISO 75-2/A | 126 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Temperature at the rear of the barrel | 50 到 80 | °C | ||
| Temperature in the middle of the barrel | 250 到 270 | °C | ||
| Temperature at the front of the material cylinder | 270 到 300 | °C | ||
| Spray nozzle temperature | 300 | °C | ||
| Back pressure | 1.47 | Mpa | ||
| Screw speed | 120 到 130 | rpm | ||
| Injection pressure | 6.37 | Mpa | ||
| Hot air dryer | 4.0 | hr | ||
| 120 | °C | |||
| Vacuum drying machine | 120 | °C | ||
| 4.0 | hr | |||
| Suggested maximum moisture content | < 0.050 | % | ||
| Mold temperature | 80 到 120 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 80 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C 6 | ISO 180/1A | 85 | kJ/m² |
| 23°C, 6.35 mm | ASTM D256 | 150 | J/m | |
| 23°C, 3.18 mm | ASTM D256 | 880 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R -Sale | ISO 2039-2 | 120 | |
| R-Scale | ASTM D785 | 120 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 2.6 to 3.2 mm | UL 94 | HB | |
| 1.6 to 2.0 mm | UL 94 | V-2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.