Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ISO1183/B | 1.20 | g/cm³ |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| Meltvolume-flowrate | 300°C/1.2kg | ISO11332 | 9.00 | cm3/10min |
| Shrinkage rate | MD | ISO294-4 | 0.50to0.70 | % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.15 | % |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.32 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2/50 | 2300 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 60.0 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 70.0 | Mpa |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Tensile strain | Break | ISO527-2/50 | 150 | % |
| Taber abraser | | ISO9352 | 45 | % |
| Bending modulus 3 | | ISO178 | 2400 | Mpa |
| Bending stress 3 | | ISO178 | 97.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Annealed | ISO75-2/B | 144 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 125 | °C |
| Hot deformation temperature | 1.8MPa,Annealed | ISO75-2/A | 141 | °C |
| Vicat softening temperature | | ISO306/B50 | 149 | °C |
| Ball pressure temperature | | IEC60335-1 | >125 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Dielectric strength | | IEC60243-1 | 17 | KV/mm |
| Dielectric constant | 60Hz | IEC60250 | 3.00 | |
| Dielectric constant | 1MHz | IEC60250 | 3.00 | |
| Relative permittivity | 100Hz | IEC60250 | 3.00 | |
| Relative permittivity | 1MHz | IEC60250 | 3.00 | |
| Dissipation factor | 50Hz | IEC60250 | 1E-03 | |
| Dissipation factor | 1MHz | IEC60250 | 2E-03 | |
| Compared to the anti leakage trace index | 2.00mm,SolutionA | IEC60112 | 250 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 13 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 35 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/A | 90 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Sale | ISO2039-2 | 73 | |
| Rockwell hardness | R-Sale | ISO2039-2 | 118 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index | | ISO489 | 1.586 | |
| Transmittance 5 | | ASTMD1003 | 89.0 | % |
| Haze 5 | | ASTMD1003 | 1.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating 5 | 1.5mm | UL94 | HB | |
| UL flame retardant rating 5 | 3.0mm | UL94 | HB | |
| GlowWireFlammability Index4 | 1.0mm | IEC60695-2-12 | 900 | °C |
| GlowWireFlammability Index4 | 2.0mm | IEC60695-2-12 | 875 | °C |
| GlowWireFlammability Index4 | 3.0mm | IEC60695-2-12 | 875 | °C |
| Hot filament ignition temperature 4 | 1.0mm | IEC60695-2-13 | 800 | °C |
| Hot filament ignition temperature 4 | 2.0mm | IEC60695-2-13 | 775 | °C |
| Hot filament ignition temperature 4 | 3.0mm | IEC60695-2-13 | 775 | °C |
| Extreme Oxygen Index 4 | | ISO4589-2 | 26 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.