PP CELSTRAN® PP-GF60-0403 CELANESE NANJING
21
- Unit Price:
- $1528 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance High temperature resistan
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- | ISO527-2/1A/1 | 15000 | Mpa |
| 80°C | ISO527-2/1A | 9500 | Mpa | |
| Bending modulus | 23°C | ISO178 | 16000 | Mpa |
| 80°C | ISO178 | 11000 | Mpa | |
| Tensile stress | Break | ISO527-2/1A/5 | 145 | Mpa |
| 80°C | ISO527-2/1A | 85.0 | Mpa | |
| Tensile strain | Break | ISO527-2/1A/5 | 1.5 | % |
| Break,80°C | ISO527-2/1A | 2.0 | % | |
| Bending stress | 23°C | ISO178 | 240 | Mpa |
| 80°C | ISO178 | 136 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature 2 | ISO11357-3 | 168 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 160 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 70 | kJ/m² |
| 23°C | ISO179/1eU | 68 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.