PP Daplen™ EF341AE BOREALIS EUROPE
128
- Unit Price:
- $1528 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Easy to process High surface finish Low shrinkage Filler mineral filler 3
- Application Areas:Automotive External Parts Automotive External Parts
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | --2 | 内部方法 | 0.75 | % |
| 90°C,2小时 | 内部方法 | 0.10 | % | |
| Melt mass flow rate | 230°C/2.16kg | ISO1133 | 15 | g/10min |
| density | ISO1183 | 1.15 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | ISO178 | 37.0 | Mpa | |
| Tensile stress | 屈服 | ISO527-2/50 | 25.0 | Mpa |
| Tensile strain | 屈服 | ISO527-2/50 | 2.6 | % |
| 断裂 | ISO527-2/50 | 20 | % | |
| Tensile modulus | ISO527-2/1 | 3100 | Mpa | |
| Bending modulus | ISO178 | 3300 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 70.0 | °C |
| 0.45MPa,未退火 | ISO75-2/B | 123 | °C | |
| Vicat softening temperature | -- | ISO306/A50 | 150 | °C |
| -- | ISO306/B50 | 64.0 | °C | |
| Linear coefficient of thermal expansion | MD：-30到80°C | 内部方法 | 5.4E-05 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 7.5 | kJ/m² |
| -20°C | ISO179/1eA | 2.5 | kJ/m² | |
| -30°C | ISO179/1eA | 2.4 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 9.0 | kJ/m² |
| -20°C | ISO180/1A | 2.8 | kJ/m² | |
| Impact strength of simply supported beam without notch | -20°C | ISO179/1eU | 29 | kJ/m² |
| 23°C | ISO179/1eU | 63 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H132/10 | ISO2039-1 | 63.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.