PP Daplen™ FS65T20 BOREALIS EUROPE
133
- Unit Price:
- $1528 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Mineral reinforcement enhance
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear forming shrinkage rate | Flow，150x80x20 | Borealis Method | 0.009 | cm/cm |
| Transverse，150x80x20 | Borealis Method | 0.01 | cm/cm |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ball indentation hardness | H385/30 | ISO 2039 | 82 | Mpa |
| tensile strength | 50mm/min | ISO 527-2 | 32 | Mpa |
| elongation | ISO 527-2 | 4.9 | % | |
| Bending modulus | 5mm/min | ISO 178 | 2800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.46MPa | ISO 75-2 | 121 | °C |
| 1.8MPa | ISO 75-2 | 60 | °C | |
| vicat softening point | A(10N) | ISO 306 | 154 | °C |
| B(50N) | ISO 306 | 89 | °C | |
| Melting temperature | Polymer Mass Temp | 210-260 | °C | |
| Mold temperature | 30-60 | °C |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO 1183 | 1.04 | g/cm | |
| Melt index | 230℃，5kg | ISO 1133 | 26 | g/10min |
| 230℃，2.16kg | ISO 1133 | 6 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.