PP 8650 TOTAL USA
100
- Unit Price:
- $1528 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Withdrawal level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23℃ | g/cm³ | 0.891到0.910 | ||
| -- | g/cm³ | 0.900 | ||
| 230°C/2.16kg | g/10min | 0.20到28 | ||
| 23℃ | % | 1.5 | ||
| Melt volume flow rate | 230°C/2.16kg | ISO 527-2/5, ISO 527-2/50 | 0.01到0.25 | |
| 230°C/2.16kg | g/10min | 0.25到38 | ||
| SpiralFlow | mm | 500.38到800.10 | ||
| Flow: 23 ℃ | mm/mm | 0.330到0.457 | ||
| Apparent density | g/cm³ | 0.52到0.53 | ||
| -- | 0.900到0.904 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23℃ | MPa | 572.41到1255.17 | ||
| MPa | 765.52到1268.97 | |||
| Yield, 23 ℃ | % | 6.0到28 | ||
| MPa | 19.59到31.38 | |||
| Tensile modulus | 摩擦系数 | 0.15到1.0 | ||
| 23℃ | MPa | 793.1到1303.45 | ||
| Yield, 23 ℃ | MPa | 24.41到30.48 | ||
| 23℃ | MPa | 889.66到1200.0 | ||
| Fracture, 23 ℃ | % | 78到510 | ||
| MPa | 19.31到44.34 | |||
| % | 46到510 | |||
| Bending stress | 23℃ | MPa | 6.5到25.03 | |
| Fracture, 23 ℃ | MPa | 14.48到40.0 | ||
| Yield, 23 ℃ | % | 10到16 | ||
| Obvious bending modulus | 23℃ | MPa | 737.93到827.59 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 0.45MPa, unannealed | °C | 54到85 | ||
| -- | °C | 65到136 | ||
| °C | 125到148 | |||
| °C | 125到150 | |||
| °C | 124到139 | |||
| °C | 132到150 | |||
| °C | 140到150 | |||
| 1.8MPa, unannealed | °C | 48到55 | ||
| -- | °C | 127到150 | ||
| 0.45MPa, unannealed | °C | 72到100 | ||
| 1.8MPa, unannealed | °C | 45到96 |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| MD: yield | MPa | 18.0到22.62 | ||
| 23℃ | MPa | 25.03到42.48 | ||
| MD | MPa | 344.83到793.1 | ||
| Film thickness - tested | 2.0到3.1 | |||
| Fracture, 23 ℃ | % | 500到760 | ||
| 23℃ | MPa | 190.34到800.0 | ||
| Fracture, 23 ℃ | MPa | 29.03到39.59 | ||
| MD: crack | MPa | 20.34到40.55 | ||
| % | 490到760 | |||
| Dart impact equipped with measuring instruments | 23℃ | J | 0.54到16.45 | |
| Initial sealing temperature | °C | 105到115 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23℃ | kJ/m² | 0.744到2.089 | ||
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 1.114到45.037 | |
| Cantilever beam without notch impact strength | 23℃ | J/m | 0.013到0.024 | |
| Falling hammer impact | 23℃ | N.m | 1831.86到2831.86 | |
| 23℃ | J/m | 0.009到0.028 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23℃ | 52到80 | |||
| Shore hardness | 23℃ | 75到98 | ||
| Rockwell hardness | 23℃ | 58到68 | ||
| Ball pressure hardness | MPa | 44.83到60.0 | ||
| 23℃ | 79到100 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | % | 0.40到17 | ||
| gloss | 79到132 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.