Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate - flow | | ASTM D955 | 0.20 到 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | | ISO 527-2 | 130 | Mpa |
| Bending modulus | | ISO 178 | 11000 | Mpa |
| Bending stress | | ISO 178 | 205 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 155 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | 内部方法 | 4.0E+2 | ohms |
| Volume resistivity | | 内部方法 | 1.0E+2 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 80 到 120 | °C |
| drying time | | | 3.0 到 5.0 | hr |
| Temperature at the rear of the barrel | | | 190 到 230 | °C |
| Temperature in the middle of the barrel | | | 220 到 240 | °C |
| Temperature at the front of the material cylinder | | | 240 到 250 | °C |
| Spray nozzle temperature | | | 230 到 250 | °C |
| Mold temperature | | | 60 到 80 | °C |
| Back pressure | | | 5.00 到 20.0 | Mpa |
| Screw speed | | | 50 到 90 | rpm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.2 mm, Black | UL 94 | V-1 | |
| UL flame retardant rating | 1.5 mm, Black | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.