OBC INFUSE™ 9077 DOW USA
120
- Unit Price:
- $3141 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 66MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Withdrawal level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 0.50 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus -100% secant | Compression Molded | ASTMD638 | 1.21 | Mpa |
| Tensile strength | Break,Compression Molded | ASTMD638 | 3.00 | Mpa |
| elongation | Break,Compression Molded | ASTMD638 | >1000 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glass transition temperature | 内部方法 | -65.0 | °C | |
| Melting temperature (DSC) | 内部方法 | 118 | °C | |
| TMA | 内部方法 | 108 | °C |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tear strength 1 | ASTMD624 | 26.3 | kN/m | |
| Permanent compression deformation | 23°C | ASTMD395 | 20 | % |
| 70°C | ASTMD395 | 43 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore A,Compression Molded | ASTMD2240 | 51 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.