Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass Flow Rate (MFR) 220 ℃/10 kg | / | ASTM D 1238 | 20.621 | g/10 min |
| Melt flow rate | 220°C/10.0 kg | ASTM D1238 | 21 | g/10 min |
| Shrinkage rate - flow | 23°C, 3.20 mm, Injection | ASTM D955 | 0.40 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength yield (yld) | 3.2mm, 5 | ASTM D638 | 470 | kg/cm2 |
| Tensile elongation fracture (brk) | 3.2mm, 5 | ASTM D638 | 30 | % |
| bending strength | 3.2mm, 1 | ASTM D790 | 700 | kg/cm2 |
| Bending modulus | 3.2mm, 1 | ASTM D790 | 22000 | kg/cm2 |
| Tensile modulus | 23°C, 3.20 mm, Injection | ASTM D638 | 2050 | Mpa |
| Tensile strength | Yield, 23°C, 3.20 mm, Injection | ASTM D638 | 48.0 | Mpa |
| Elongation rate 4 | Yield, 23°C, 3.20 mm, Injection | ASTM D638 | > 5.0 | % |
| Elongation rate 4 | Break, 23°C, 3.20 mm, Injection | ASTM D638 | 15 | % |
| Bending modulus | 23°C, 3.20 mm, Injection | ASTM D790 | 2250 | Mpa |
| bending strength | 23°C, 3.20 mm, Injection | ASTM D790 | 71.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Thermal deformation temperature under load | 1.8 MPa, Unannealed, 6.40 mm, Injection | ASTM D648 | 81.0 | °C |
| Vicat softening temperature | | ASTM D15257 | 89.0 | °C |
| RTI Elec | | UL 746 | 50.0 | °C |
| RTI Imp | | UL 746 | 50.0 | °C |
| RTI | | UL 746 | 50.0 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 80 到 90 | °C |
| drying time | | | 2.0 到 4.0 | hr |
| Temperature at the rear of the barrel | | | 180 到 200 | °C |
| Temperature in the middle of the barrel | | | 190 到 210 | °C |
| Temperature at the front of the material cylinder | | | 200 到 220 | °C |
| Spray nozzle temperature | | | 190 到 220 | °C |
| Processing (melt) temperature | | | 190 到 220 | °C |
| Mold temperature | | | 40 到 60 | °C |
| Back pressure | | | 29.4 到 58.8 | Mpa |
| Screw speed | | | 30 到 60 | rpm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Izod Notched at 23 ℃ (73 ℉) | 3.2mm | ASTM D256 | 17 | kg·cm/cm |
| Izod Notched at 23 ℃ (73 ℉) | 6.4mm | ASTM D256 | 17 | kg·cm/cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness R | | | 107 | |
| Rockwell hardness | R-Scale, 23°C, Injection | ASTM D785 | 107 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| transmissivity | 3200 μm, Injection | ASTM D1003 | 90.0 | % |
| Haze | Injection | ASTM D1003 | 2.0 | % |
| Light transmittance |
Rate B/50 | ASTM D1003 | 90 | % |
| Haze | -40°C to | ASTM D1003 | 2 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB | |
| UL flame retardant rating | 3.0 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.