ABS/PMMA STAREX® BF-0670 BK22101 Samsung Cheil South Korea
226
- Unit Price:
- $2336 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 31MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Aging resistance High impact resistance
- Application Areas:Electrical appliances Electronic and electrical Automotive components Lighting fixtures
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 25 | g/10min |
| 220°C/10.0kg | ISO1133 | 24 | g/10min | |
| Shrinkage rate | MD：3.20mm | ASTMD955 | 0.30 | % |
| TD：3.20mm | ASTMD955 | 0.30 | % | |
| TD:3.20mm | ISO2577 | 0.40 | % | |
| MD:3.20mm | ISO2577 | 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTMD638 | 2080 | Mpa | |
| Tensile modulus | ISO527-2/50 | 2500 | Mpa | |
| Tensile strength 2 | Yield | ASTMD638 | 49.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 52.0 | Mpa |
| Tensile strength 2 | Break | ASTMD638 | 36.3 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 36.0 | Mpa |
| Elongation rate 2 | Break | ASTMD638 | 18 | % |
| Tensile strain | Break | ISO527-2/50 | 22 | % |
| Bending modulus 3 | ASTMD790 | 2350 | Mpa | |
| Bending modulus 4 | ISO178 | 2360 | Mpa | |
| Bending strength 3 | ASTMD790 | 66.7 | Mpa | |
| Bending stress 4 | ISO178 | 70.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 80.0 | °C |
| 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 72.0 | °C | |
| 1.8MPa,Annealed,4.00mm | ISO75-2/A | 86.0 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 92.090.0 | °C |
| -- | ISO306/B120 | 92.0 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 90.0 | °C |
| 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 83.0 | °C | |
| 0.45MPa,Annealed,4.00mm | ISO75-2/B | 92.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 8.0 | kJ/m² |
| Suspended wall beam gap impact strength 5 | 23°C | ISO180/1A | 7.4 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 114 | |
| R-Scale | ISO2039-2 | 115 | ||
| PencilHardness | --6 | JISK5401 | F | |
| --7 | JISK5401 | F |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 2.0mm | UL94 | HB | ||
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.