POM/PTFE LNP™ LUBRICOMP™ KL-4540-NAT SABIC INNOVATIVE US
244
Unit Price:$5858 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low extract Internal lubrication
- Application Areas:Medical and nursing suppl Electrical appliances Plastic bag
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 流动 : 24小时 | ASTM D955 | 2.1 到 2.9 | % |
| 横向流动 : 24小时 | ASTM D955 | 2.1 到 2.9 | % | |
| 吸水率 | 24 hr, 50% RH | ASTM D570 | 0.18 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.43 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 弯曲应力 | -- | ISO 178 | 60.0 | Mpa |
| 断裂, 50.0 mm 跨距 3 | ASTM D790 | 63.0 | Mpa | |
| 拉伸模量 | -- 1 | ASTM D638 | 1830 | Mpa |
| -- | ISO 527-2/1 | 2020 | Mpa | |
| 伸长率 | 屈服 2 | ASTM D638 | 14 | % |
| 屈服 | ISO 527-2/5 | 22 | % | |
| 断裂 2 | ASTM D638 | 30 | % | |
| 断裂 | ISO 527-2/5 | 43 | % | |
| 弯曲模量 | 50.0 mm 跨距 3 | ASTM D790 | 2020 | Mpa |
| -- 4 | ISO 178 | 2080 | Mpa | |
| 抗张强度 | 屈服 2 | ASTM D638 | 43.0 | Mpa |
| 屈服 | ISO 527-2/5 | 39.0 | Mpa | |
| 断裂 2 | ASTM D638 | 43.0 | Mpa | |
| 断裂 | ISO 527-2/5 | 39.0 | Mpa | |
| 摩擦系数 5 | Dynamic | ASTM D3702 | 0.25 | |
| Static | ASTM D3702 | 0.14 | ||
| 磨损因数 5 | ASTM D3702 | 1.8E+6 | 10^-8 mm³/N·m |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 载荷下热变形温度 | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 87.0 | °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 6 | ISO 75-2/Af | 79.0 | °C | |
| 线形热膨胀系数 | 流动 : -40 到 40°C | ASTM E831 | 1.1E-4 | cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 1.1E-4 | cm/cm/°C |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 80 | °C | ||
| 加工（熔体）温度 | 200 到 215 | °C | ||
| 模具温度 | 80 到 110 | °C | ||
| 干燥时间 | 4.0 | hr | ||
| 料筒后部温度 | 175 到 190 | °C | ||
| 料筒中部温度 | 195 到 205 | °C | ||
| 料筒前部温度 | 210 到 220 | °C | ||
| 背压 | 0.200 到 0.300 | Mpa | ||
| 螺杆转速 | 30 到 60 | rpm |
| 冲击性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 装有测量仪表的落镖冲击 | 23°C, Energy at Peak | ASTM D3763 | 3.00 | J |
| -- | ISO 6603-2 | 1.00 | J | |
| 无缺口悬臂梁冲击 | 23°C | ASTM D4812 | 620 | J/m |
| 23°C 6 | ISO 180/1U | 42 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.