PC/PTFE LNP™ LUBRILOY™ D20001-8T8D029L SABIC INNOVATIVE US
202
- Unit Price:
- $8527 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 18MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:wear resistant
- Application Areas:Electrical appliances Electronic display Aerospace Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissolved Volume Flow Rate (MVR) | 300°C/1.2 kg | ASTM D1238 | 15.7 | cm3/10min |
| Shrinkage rate | Flow : 24hr | ASTM D955 | 0.50 | % |
| Across Flow : 24hr | ASTM D955 | 0.60 | % | |
| Across Flow : 24hr | ISO 294-4 | 0.57 | % | |
| 流量 : 24hr | ISO 294-4 | 0.53 | % | |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.12 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 2 | ASTM D638 | 2550 | Mpa |
| -- | ISO 527-2/1 | 2600 | Mpa | |
| Tensile strength | Yield | ASTM D638 | 67.0 | Mpa |
| Yield | ISO 527-2 | 62.0 | Mpa | |
| Break | ASTM D638 | 60.0 | Mpa | |
| Break | ISO 527-2 | 54.0 | Mpa | |
| elongation | Yield | ASTM D638 | 4.5 | % |
| Yield | ISO 527-2 | 4.3 | % | |
| Break | ASTM D638 | 6.5 | % | |
| Break | ISO 527-2 | 6.7 | % | |
| Bending modulus | -- | ASTM D790 | 2820 | Mpa |
| -- | ISO 178 | 2800 | Mpa | |
| bending strength | -- | ASTM D790 | 103 | Mpa |
| -- | ISO 178 | 102 | Mpa | |
| Friction coefficient 3 | Dynamic | ASTM D3702 | 0.090 | |
| Static | ASTM D3702 | 0.22 | ||
| Wear factor 3 | ASTM D3702 | 6.0E+6 | 10^-8 mm³/N·m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 97.0 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 89.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 4 | ISO 75-2/Af | 94.0 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 6.6E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 6.7E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 6.7E-5 | cm/cm/°C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| drying time | 4.0 到 6.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Temperature at the rear of the barrel | 250 到 260 | °C | ||
| Temperature in the middle of the barrel | 255 到 265 | °C | ||
| Temperature at the front of the material cylinder | 260 到 270 | °C | ||
| Processing (melt) temperature | 255 到 290 | °C | ||
| Mold temperature | 40 到 65 | °C | ||
| Back pressure | 0.200 到 0.300 | Mpa | ||
| Screw speed | 30 到 60 | rpm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 1600 | J/m |
| 23°C 4 | ISO 180/1U | 100 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C, Energy at Peak | ASTM D3763 | 51.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm, Testing by SABIC | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.