Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 190°C/10.0kg | JISK7210 | 7.0 | g/10min |
| SpiralFlow | | 内部方法 | 33.0 | CM |
| Shrinkage rate | MD:2.00mm | 内部方法 | 1.5 | % |
| Shrinkage rate | TD:2.00mm | 内部方法 | 1.3 | % |
| Water absorption rate | 24hr | ASTMD570 | <0.010 | % |
| PVLimit3 | | 内部方法 | >0.50 | MPa·m/s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength 4 | Break,23°C | ASTMD638 | 47.0 | Mpa |
| Elongation rate 4 | Break,23°C | ASTMD638 | 9.0 | % |
| Bending modulus 5 | 23°C,3.00mm,48.0mmSpan | ASTMD790 | 2300 | Mpa |
| Bending strength 5 | 23°C,3.00mm,48.0mmSpan | ASTMD790 | 45.0 | Mpa |
| Friction coefficient 3 | Dynamic | 内部方法 | 0.17 | |
| Wear amount 3 | | 内部方法 | 220 | 10^-8mm³/N·m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 91.0 | °C |
| Vicat softening temperature | | ASTMD15256 | 130 | °C |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1.2E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | ASTMD257 | 1.0E+17到1.0E+18 | ohms·cm |
| Dielectric strength | | ASTMD149 | 60 | KV/mm |
| Dielectric constant | 23°C | ASTMD150 | 2.50 | |
| Dissipation factor | 1MHz | ASTMD150 | 1.0E-4到2.0E-4 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 63 | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| HeatGenerationTemperature3 | | 内部方法 | 75 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.