PBT/PET VALOX™ 8032UX BK1A404U SABIC INNOVATIVE US
216
- Unit Price:
- $3662 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Filler: Glass fiber reinf 30% Filler by weight
- Application Areas:Handle packing Home appliance components Shell
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| -- | ASTMD792 | 1.58 | g/cm³ | |
| ISO1183 | 1.53 | g/cm³ | ||
| Melt mass flow rate | 265°C/2.16kg | ASTMD1238 | 15 | g/10min |
| Melt volume flow rate | 265°C/2.16kg | ISO1133 | 15.0 | cm3/10min |
| Shrinkage rate | MD1 | 内部方法 | 0.40到0.80 | % |
| MD:3.20mm | 内部方法 | 0.40到0.80 | % | |
| TD2 | 内部方法 | 0.60到1.0 | % | |
| TD:3.20mm | 内部方法 | 0.60到1.0 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.16 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.050 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| crack | ISO527-2/5 | 2.5 | % | |
| 50.0mm span 8 | ASTMD790 | 8450 | Mpa | |
| --9 | ISO178 | 8500 | Mpa | |
| --10 | ISO178 | 210 | Mpa | |
| Yield, 50.0mm span 11 | ASTMD790 | 165 | Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 30.0 | mg |
| --3 | ASTMD638 | 9950 | Mpa | |
| Surrender 4 | ASTMD638 | 115 | Mpa | |
| yield | ISO527-2/5 | 145 | Mpa | |
| Fracture 5 | ASTMD638 | 115 | Mpa | |
| crack | ISO527-2/5 | 145 | Mpa | |
| Surrender 6 | ASTMD638 | 2.0 | % | |
| yield | ISO527-2/5 | 2.4 | % | |
| Fracture 7 | ASTMD638 | 2.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flow: 23 to 60 ° C | ISO11359-2 | 2.2E-05 | cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 7.5E-05 | cm/cm/°C | |
| Horizontal: 23 to 60 ° C | ISO11359-2 | 8.1E-05 | cm/cm/°C | |
| 0.45MPa, unannealed, 3.20mm | ASTMD648 | 208 | °C | |
| 0.45MPa, unannealed, 100mm span 19 | ISO75-2/Be | 217 | °C | |
| 1.8MPa, unannealed, 3.20mm | ASTMD648 | 190 | °C | |
| 1.8MPa, unannealed, 100mm span 20 | ISO75-2/Ae | 195 | °C | |
| -- | ISO 8958-1998 | 202 | °C | |
| ASTMD1525,ISO306/A501222 | 220 | °C | ||
| ISO306/B120 | 204 | °C | ||
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Flow: -40 to 40 ° C | ASTME831 | 2.5E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | 0.800mm,in Oil | IEC60243-1 | 27 | KV/mm |
| 1.60mm,in Oil | IEC60243-1 | 23 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 15 | KV/mm | |
| Relative permittivity | 50Hz | IEC60250 | 3.30 | |
| 60Hz | IEC60250 | 3.30 | ||
| 100Hz | IEC60250 | 3.60 | ||
| 1MHz | IEC60250 | 3.20 | ||
| Dissipation factor | 50Hz | IEC60250 | 8E-04 | |
| 60Hz | IEC60250 | 8E-04 | ||
| 1MHz | IEC60250 | 0.013 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| Leakage Trace Index | IEC60112 | 300 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| -30°C | ASTMD256 | 48 | J/m | |
| 23°C | ASTMD256 | 57 | J/m | |
| -30°C14 | ISO180/1A | 8.0 | kJ/m² | |
| 0°C15 | ISO180/1A | 8.0 | kJ/m² | |
| 23°C16 | ISO180/1A | 9.0 | kJ/m² | |
| -30°C | ASTMD4812 | 470 | J/m | |
| 23°C | ASTMD4812 | 480 | J/m | |
| -30°C17 | ISO180/1U | 40 | kJ/m² | |
| 23°C18 | ISO180/1U | 45 | kJ/m² | |
| Impact strength of simply supported beam gap 12 | -30°C | ISO179/1eA | 9.0 | kJ/m² |
| 23°C | ISO179/1eA | 9.0 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is 13 | -30°C | ISO179/1eU | 40 | kJ/m² |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 8.00 | J |
| The impact strength of a simply supported beam without a notch is 13 | 23°C | ISO179/1eU | 45 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale | ISO2039-2 | 119 | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 110 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.60mm,TestingbySABIC | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.