PA/ABS Terblend®N N NM-19 BASF USA
190
- Unit Price:
- $6468 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance Easy to process High mobility High impact resistance
- Application Areas:Low temperature applicati Automotive sector Automotive interior parts sporting goods
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 240°C/10.0kg | ISO1133 | 25.0 | cm3/10min |
| Shrinkage rate | ISO294-4 | 0.80 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 1.1 | % |
| Melt volume flow rate | 240°C/10.0kg | ISO1133 | 30.0 | cm3/10min |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 1.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 2000 | Mpa | |
| ISO527-2 | 1600 | Mpa | ||
| Tensile stress | Yield,23°C | ISO527-2 | 35.0 | Mpa |
| Tensile strain | Yield,23°C | ISO527-2 | 3.4 | % |
| Bending modulus | ISO178 | 1500 | Mpa | |
| Bending stress | ISO178 | 50.0 | Mpa | |
| Tensile stress | Yield,23°C | ISO527-2 | 43.0 | Mpa |
| Tensile strain | Yield,23°C | ISO527-2 | 3.5 | % |
| Bending modulus | ISO178 | 1800 | Mpa | |
| Bending stress | ISO178 | 62.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 2 | 0.45MPa,Annealed | ISO75-2/B | 80.0 | °C |
| 1.8MPa,Annealed | ISO75-2/A | 58.0 | °C | |
| Vicat softening temperature | -- | ISO306/A50 | 165 | °C |
| -- | ISO306/B50 | 91.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Hot deformation temperature 2 | 1.8MPa,Annealed | ISO75-2/A | 65.0 | °C |
| Vicat softening temperature | -- | ISO306/A50 | 160 | °C |
| -- | ISO306/B50 | 102 | °C | |
| Hot deformation temperature 2 | 0.45MPa,Annealed | ISO75-2/B | 85.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Relative permittivity | 1MHz | IEC60250 | 2.90 | |
| Dissipation factor | 1MHz | IEC60250 | 0.015 | |
| Leakage Trace Index | IEC60112 | 600 | V |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation MD | Break | ISO527-3 | >50 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ISO2039-2 | 103 | |
| Ball pressure hardness | ISO2039-1 | 86.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.