PVDF Kynar® Kynar 741 ARKEMA FRANCE
185
- Unit Price:
- $14708 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | ASTM D1238 | 6.0 到 25 | g/10min | |
| Apparent viscosity of melt | 232℃，100 sec^-1 232℃，100 sec^-1 | ASTM D3835 | 1500 到 2300 | Pa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D，23℃ Shore D，23℃ | ASTM D2240 | 76 到 80 | |
| Tensile strength | Yield，23℃ Yield, 73°F | 44.8 到 55.2 | Mpa | |
| Break，23℃ Break, 73°F | 34.5 到 55.2 | Mpa | ||
| Tensile strain | Break，23℃ Break，23℃ | ASTM D638 | 20 到 100 | % |
| Bending modulus | 23℃ 23℃ | ASTM D790 | 1380 到 2310 | Mpa |
| bending strength | 23℃ 23℃ | ASTM D790 | 58.6 到 75.8 | Mpa |
| compressive strength | 23℃ 23℃ | ASTM D695 | 68.9 到 103 | Mpa |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | 20 ℃ 20℃ 1 | ASTM D257 | 200000000000000 | ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Peak melting temperature | ASTM D3418 | 165 到 172 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.