PVDF SOLEF® 20810-55 SOLVAY USA
117
- Unit Price:
- $7303 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high viscosity
- Application Areas:film adhesive
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Specific gravity | ISO 1183 | 1.78 | g/cm³ | |
| Shrinkage rate flow | ASTM D995 | 2 | % | |
| Vertical shrinkage rate | ASTM D995 | 3 | % | |
| Water absorption rate at 23 ° C for 24 hours | ISO 62 | 0.04 | % | |
| Melt index 230 ° C 2.16kg | ASTM D1238 | 2 | g/10min | |
| Melt index 230 ° C 5kg | ASTM D1238 | 6 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus at 23 ° C 1.0mm/min | ASTM D638 | 420 | Mpa | |
| Tensile strength at 23 ° C 50mm/min | ASTM D638 | 40 | Mpa | |
| Tensile strength yielding at 23 ° C | ASTM D638 | 16.5 | Mpa | |
| Elongation at 23 ° C | ASTM D638 | 675 | % | |
| Elongation yield at 23 ° C 50mm/min | ASTM D638 | 13.5 | % | |
| Bending strength at 23 ° C | ASTM D790 | 40 | Mpa | |
| Bending modulus at 23 ° C | ASTM D790 | 400 | Mpa | |
| Cantilever beam notch impact at 23 ° C | ASTM D256 | 180 | J/m | |
| Friction coefficient dynamics | ASTM D3702 | 0.25 | ||
| Static friction coefficient | ASTM D3702 | 0.3 | ||
| Tiber wear and tear | 10 | mg/1000cy |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature annealing 4.0mm | ASTM D648 | 62 | °C | |
| ASTM D648 | 40 | °C | ||
| Vicat softening temperature 50 ° C/hr 10N | ISO 306 | 120 | °C | |
| Melting temperature | ASTM D3418 | 135 | °C | |
| Glass transition temperature | -29 | °C | ||
| Brittle temperature | ASTM D746 | -22 | °C | |
| Thermal conductivity coefficient | JIS R2618 | 0.18 | W/(m·K) | |
| Specific heat capacity | 1200 | J/(kg·°C) | ||
| Specific heat capacity 100 ° C | 1600 | J/(kg·°C) | ||
| Crystallization temperature | 92 | |||
| Average heat of fusion | 23 | J/g | ||
| 24 | J/g |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistance | ASTM D257 | 100000000000000 | Ω | |
| Oxygen index | ASTM D2863 | 54.5 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| hardness | 测试标准 | 数据 | 单位 | |
| Shore hardness D 2.0mm | ASTM D2240 | 60 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.