PC/PET XYLEX™ HX7509HP SABIC INNOVATIVE US
221
- Unit Price:
- $3754 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High heat resistance
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 265°C/2.16kg | ASTMD1238 | 12 | g/10min |
| Melt volume flow rate | 265°C/2.16kg | ISO1133 | 11.5 | cm3/10min |
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.40到0.60 | % |
| TD:3.20mm | 内部方法 | 0.50到0.70 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.12 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.050 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | --3 | ASTMD638 | 2150 | Mpa |
| -- | ISO527-2/1 | 2300 | Mpa | |
| Tensile strength | Yield4 | ASTMD638 | 60.0 | Mpa |
| Yield | ISO527-2/50 | 60.0 | Mpa | |
| Break4 | ASTMD638 | 63.0 | Mpa | |
| Break | ISO527-2/50 | 62.0 | Mpa | |
| elongation | Yield4 | ASTMD638 | 6.3 | % |
| Yield | ISO527-2/50 | 5.8 | % | |
| Break4 | ASTMD638 | 140 | % | |
| Break | ISO527-2/50 | 130 | % | |
| Bending modulus | 50.0mmSpan5 | ASTMD790 | 2300 | Mpa |
| --6 | ISO178 | 2260 | Mpa | |
| Bending stress | --6,7 | ISO178 | 92.0 | Mpa |
| Yield,50.0mmSpan5 | ASTMD790 | 95.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 119 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 106 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan10 | ISO75-2/Af | 108 | °C | |
| Vicat softening temperature | -- | ASTM D-596 | 126 | °C |
| -- | ISO306/B50 | 125 | °C | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 1E-04 | cm/cm/°C |
| MD:-40to40°C | ISO11359-2 | 6.8E-05 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 1E-04 | cm/cm/°C | |
| TD:-40to40°C | ISO11359-2 | 6.8E-05 | cm/cm/°C | |
| thermal conductivity | ISO8302 | 0.23 | W/m/K |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 8 | 23°C | ISO179/1eA | 10 | kJ/m² |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 77.0 | J |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| transmissivity | 2540µm | ASTMD1003 | 88.0 | % |
| Haze | 2540µm | ASTMD1003 | 2.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | V-2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.