PC/PET Eastalloy™ DA003-8906K EASTMAN USA

194

Unit Price:
$3754 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
12MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD：3.20mm	ASTMD955	0.50to0.70	%
Water absorption rate	24hr	ASTMD570	0.13	%
Water absorption rate	Water absorption rate	23°C,24hr	ISO62	0.13	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
bending strength	4.00mm	ISO178	81.0	Mpa
bending strength	bending strength	Yield	ASTMD790	86.0	Mpa
Tensile strength	Yield	ASTMD638	56.0	Mpa
Tensile stress	Yield,4.00mm	ISO527-2	56.0	Mpa
Tensile strength	Break	ASTMD638	60.0	Mpa
Tensile stress	Break,4.00mm	ISO527-2	56.0	Mpa
elongation	Yield	ASTMD638	6.0	%
TensileStrain	Yield,4.00mm	ISO527-2	5.4	%
elongation	Break	ASTMD638	150	%
Tensile strain	Break,4.00mm	ISO527-2	130	%
Bending modulus		ASTMD790	2140	Mpa
Bending modulus	Bending modulus	4.00mm	ISO178	2100	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
specific heat	60°C	DSC	1380	J/kg/°C
specific heat	specific heat	240°C	DSC	2180	J/kg/°C
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	103	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	103	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	90.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	90.0	°C
Vicat softening temperature		ASTMD15252	118	°C
	Vicat softening temperature	--	ISO306/A	118	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO306/B	110	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Leakage Trace Index		ASTMD3638	>600	V
High voltage arc tracing rate	HVTR	UL746	38.0	mm/min
Surface resistivity		ASTMD257	1E+16	ohms
Volume resistivity		ASTMD257	1E+15	ohms·cm
Dielectric strength 3		ASTMD149	17	KV/mm
Dielectric constant	1kHz	ASTMD150	2.30
Dielectric constant	Dielectric constant	1MHz	ASTMD150	2.10
Dissipation factor	1kHz	ASTMD150	2E-03
Dissipation factor	Dissipation factor	1MHz	ASTMD150	8E-03
Arc resistance		ASTMD495	143	sec

Impact performance	Test Condition	Test Method	Test Result	Unit
Dart impact equipped with measuring instruments	-40°C,EnergyatPeakLoad	ASTMD3763	46.0	J
Dart impact equipped with measuring instruments	Dart impact equipped with measuring instruments	23°C,EnergyatPeakLoad	ASTMD3763	51.0	J
Multi axis Instrumented Impact Energy	-40°C,能量to力量峰值	ISO6603-2	23.0	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C,能量to力量峰值	ISO6603-2	19.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTMD785	117

optical performance	Test Condition	Test Method	Test Result	Unit
transmissivity	Total	ASTMD1003	81.0	%
transmissivity	transmissivity	Regular	ASTMD1003	77.0	%
Haze		ASTMD1003	3.6	%

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.6mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.