PC/PET XENOY™ XL1339U-BK1370 SABIC EU
113
- Unit Price:
- $3754 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High heat resistance
- Application Areas:Electronic and electrical Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 24 hr | ASTM D570 | 0.10 | % |
| Equilibrium, 23°C | ASTM D570 | 0.70 | % | |
| Equilibrium, 50% RH | ASTM D570 | 0.20 | % | |
| Molten Volume Flow Rate (MVR) | 265°C/1.2 kg | ISO 1133 | 4.00 | cm3/10min |
| Shrinkage rate 1 | Flow | 内部方法 | 0.50 到 0.80 | % |
| Across Flow | 内部方法 | 0.50 到 0.80 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | ASTM D1044 | 16.0 | mg |
| Tensile modulus 2 | ASTM D638 | 2090 | Mpa | |
| Bending stress | -- 5, 6 | ISO 178 | 80.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 94.0 | Mpa | |
| Poisson's ratio | ASTM E132 | 0.40 | ||
| Tensile strength | Yield 3 | ASTM D638 | 49.0 | Mpa |
| Yield | ISO 527-2/50 | 55.0 | Mpa | |
| Break 3 | ASTM D638 | 49.0 | Mpa | |
| Break | ISO 527-2/50 | 40.0 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 5.0 | % |
| Yield | ISO 527-2/50 | 5.0 | % | |
| Break 3 | ASTM D638 | 110 | % | |
| Break | ISO 527-2/50 | 70 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2090 | Mpa |
| -- 5 | ISO 178 | 2200 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ISO 306/A50 | 140 | °C |
| -- | ISO 306/B50 | 130 | °C | |
| -- | ISO 306/B120 | 135 | °C | |
| Linear coefficient of thermal expansion | Flow : -30 to 30°C | ASTM D696 | 7.6E-5 | cm/cm/°C |
| Across Flow : -30 to 30°C | ASTM D696 | 7.9E-5 | cm/cm/°C | |
| thermal conductivity | ASTM C177 | 0.18 | W/m/K | |
| Hot deformation temperature 9 | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 125 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 105 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 3.20 mm, in Oil | ASTM D149 | 17 | KV/mm |
| Dissipation factor | 50 Hz | ASTM D150 | 2.0E-3 | |
| 60 Hz | ASTM D150 | 2.0E-3 | ||
| 1 MHz | ASTM D150 | 0.020 | ||
| Surface resistivity | ASTM D257 | > 1.0E+15 | ohms | |
| Dielectric constant | 60 Hz | ASTM D150 | 3.30 | |
| 50 kHz | ASTM D150 | 3.30 | ||
| 1 MHz | ASTM D150 | 3.10 | ||
| Volume resistivity | ASTM D257 | > 1.0E+14 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 4.0 到 6.0 | hr | ||
| Suggested injection volume | 50 到 80 | % | ||
| Temperature at the rear of the barrel | 245 到 265 | °C | ||
| Temperature in the middle of the barrel | 250 到 270 | °C | ||
| Temperature at the front of the material cylinder | 255 到 275 | °C | ||
| Spray nozzle temperature | 255 到 270 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 50 到 80 | rpm | ||
| Exhaust hole depth | 0.013 到 0.020 | mm | ||
| drying temperature | 110 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 260 到 275 | °C | ||
| Mold temperature | 65 到 90 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 7 | -30°C | ISO 179/1eA | 35 | kJ/m² |
| 23°C | ISO 179/1eA | 45 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Unscented Izod Impact Strength 8 | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.