SPS XAREC™ C142 IDEMITSU JAPAN
224
- Unit Price:
- $3159 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 38MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced High temperature resistan
- Application Areas:Electrical applications Household daily necessiti
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.36 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.02 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | 内部方法 | 0.50to0.80 | % |
| MD | 内部方法 | 0.10to0.40 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.020 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 12600 | Mpa | |
| Tensile stress | Break | ISO527-2 | 130 | Mpa |
| Tensile strain | Break | ISO527-2 | 1.5 | % |
| Bending modulus | ISO178 | 12400 | Mpa | |
| Bending stress | ISO178 | 195 | Mpa | |
| elongation at break | ASTM D638/ISO 527 | 1.5 | % | |
| tensile strength | ASTM D638/ISO 527 | 130 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 75 | ||
| Bending modulus | ASTM D790/ISO 178 | 12.4 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 195 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB/0.80 | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 1.5 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 270 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 250 | °C | |
| Linear coefficient of thermal expansion | MD：-30to30°C | TMA | 1.5E-05 | cm/cm/°C |
| TD：-30to30°C | TMA | 4E-05 | cm/cm/°C | |
| RTIElec | UL746 | 50.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 50.0 | °C | |
| RTIStr | UL746 | 50.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | >1.0E+16 | ohms·cm | |
| Arc resistance | ASTM D495/IEC 60112 | 120 | ||
| Volume resistivity | ASTM D257/IEC 60093 | >1.0*10^16 | Ω.cm | |
| Dielectric strength | ASTMD149 | 45 | KV/mm | |
| Dielectric constant | 1MHz | IEC60250 | 3.00 | |
| Dissipation factor | 1MHz | IEC60250 | <1.0E-3 | |
| Arc resistance | ASTMD495 | PLC6 | ||
| Compared to the anti leakage trace index | CTI)3 | IEC60112 | PLC1 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod impact strength | 23°C | ISO180 | 33 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 27 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | >0.8mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.