SPS XAREC™ S931 BK IDEMITSU JAPAN
244
- Unit Price:
- $2987 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 37MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced High temperature resistan
- Application Areas:Electrical applications Household daily necessiti
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO 1183 | 1.45 | g/cm³ | |
| Shrinkage rate | Across Flow | 内部方法 | 0.30 到 0.70 | % |
| 流量 | 内部方法 | 0.10 到 0.40 | % | |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.020 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10500 | Mpa | |
| Tensile stress | Break | ISO 527-2 | 110 | Mpa |
| Tensile strain | Break | ISO 527-2 | 1.5 | % |
| Bending modulus | ISO 178 | 10300 | Mpa | |
| Bending stress | ISO 178 | 170 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 265 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 230 | °C | |
| Linear coefficient of thermal expansion | Flow : -30 to 30°C | TMA | 1.9E-5 | cm/cm/°C |
| Across Flow : -30 to 30°C | TMA | 4.2E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 130 | °C | |
| RTI Imp | UL 746 | 120 | °C | |
| RTI | UL 746 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC 60093 | > 1.0E+16 | ohms·cm | |
| Dielectric strength | ASTM D149 | 35 | KV/mm | |
| Dielectric constant | 1 MHz | IEC 60250 | 3.00 | |
| Dissipation factor | 1 MHz | IEC 60250 | 2.0E-3 | |
| Arc resistance | ASTM D495 | PLC 6 | ||
| Compared to the Leakage Tracking Index (CTI) of 4 | IEC 60112 | PLC 1 | ||
| High arc combustion index (HAI) | 0.75 mm | UL 746 | PLC 0 | |
| 1.5 mm | UL 746 | PLC 0 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 3 | ||
| Hot wire ignition (HWI) | 0.75 mm | UL 746 | PLC 3 | |
| 1.5 mm | UL 746 | PLC 2 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| drying time | 3.0 到 5.0 | hr | ||
| Processing (melt) temperature | 280 到 310 | °C | ||
| Mold temperature | 130 到 155 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 9.0 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 28 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 8.0 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO 180 | 26 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | > 0.75 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.