- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Glass fiber reinforced
- Application Areas:Electrical applications Household daily necessiti
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | 内部方法 | 0.50 到 0.80 | % |
| 流量 | 内部方法 | 0.10 到 0.40 | % | |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.020 | % |
| density | ISO 1183 | 1.41 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | ISO 178 | 170 | Mpa | |
| Tensile stress | Break | ISO 527-2 | 115 | Mpa |
| Tensile strain | Break | ISO 527-2 | 1.6 | % |
| Tensile modulus | ISO 527-2 | 10600 | Mpa | |
| Bending modulus | ISO 178 | 10000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 265 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 245 | °C | |
| RTI | UL 746 | 50.0 | °C | |
| RTI Imp | UL 746 | 50.0 | °C | |
| RTI Elec | UL 746 | 50.0 | °C | |
| Linear coefficient of thermal expansion | Flow : -30 to 30°C | TMA | 2.0E-5 | cm/cm/°C |
| Across Flow : -30 to 30°C | TMA | 4.0E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | ASTM D149 | 35 | KV/mm | |
| Compared to the Leakage Tracking Index (CTI) of 4 | IEC 60112 | PLC 1 | ||
| Dissipation factor | 1 MHz | IEC 60250 | 2.0E-3 | |
| Dielectric constant | 1 MHz | IEC 60250 | 3.00 | |
| Arc resistance | ASTM D495 | PLC 6 | ||
| Volume resistivity | IEC 60093 | > 1.0E+16 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| Processing (melt) temperature | 280 到 310 | °C | ||
| Mold temperature | 130 到 155 | °C | ||
| drying time | 3.0 到 5.0 | hr |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 28 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179 | 10 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 9.0 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO 180 | 29 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | > 1.5 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.