PC/PBT XENOY™ 5220U-7A1D383 SABIC INNOVATIVE SHANGHAI
133
- Unit Price:
- $2859 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 43MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Non enhanced Low temperature impact re Chemical resistance
- Application Areas:--
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTMD792 | 1.21 | g/cm³ | |
| Specific volume | ASTMD792 | 0.830 | cm³/g | |
| Density/specific gravity | ISO1183 | 1.22 | g/cm³ | |
| Melt mass flow rate | 250°C/5.0kg | ISO1133 | 16 | g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.80to1.0 | % |
| TD2 | 内部方法 | 0.80to1.0 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.50 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Outdoor applicability | UL746C | f2 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | --3 | ASTMD638 | 2250 | Mpa |
| --4 | ASTMD638 | 2250 | Mpa | |
| ISO527-2/1 | 2050 | Mpa | ||
| Tensile strength 6 | Yield | ASTMD638 | 53.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 50.0 | Mpa |
| Tensile strength 5 | Break | ASTMD638 | 51.0 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 50.0 | Mpa |
| Tensile strain 5 | Yield | ASTMD638 | 4.0 | % |
| Tensile strain | Yield | ISO527-2/50 | 4.0 | % |
| Tensile strain 5 | Break | ASTMD638 | 120 | % |
| Tensile strain | Break | ISO527-2/50 | 120 | % |
| Bending modulus 7 | 50.0mmSpan | ASTMD790 | 2030 | Mpa |
| ISO178 | 2000 | Mpa | ||
| Bending strength 7,8 | ISO178 | 80.0 | Mpa | |
| Bending strength 7 | Yield,50.0mmSpan | ASTMD790 | 84.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ISO306/B120 | 125 | °C |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 9.5E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 9.5E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 9E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| RTIElec | UL746 | 75.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 75.0 | °C | |
| RTIStr | UL746 | 75.0 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 107 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 84.0 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 99.0 | °C | |
| Hot deformation temperature 11 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 75.0 | °C |
| Vicat softening temperature | ASTMD152512 | 122 | °C | |
| -- | ISO306/B50 | 120 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC0 | |
| Hot wire ignition | HWI | UL746 | PLC3 | |
| Arc resistance 13 | ASTMD495 | PLC5 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC1 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CharpyNotchedImpactStrength9 | 23°C | ISO179/1eA | 55 | kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ASTMD256 | 300 | J/m |
| -30°C | ASTMD256 | 530 | J/m | |
| 23°C | ASTMD256 | 710 | J/m | |
| Suspended wall beam gap impact strength 10 | -30°C | ISO180/1A | 30 | kJ/m² |
| 23°C | ISO180/1A | 50 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 60.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.