PC/PBT XENOY™ HX6600HP 8H4D023 SABIC INNOVATIVE US
117
- Unit Price:
- $3013 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 29MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High impact resistance Dimensional stability
- Application Areas:Automotive Applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 11 | g/10min |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 10.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 1.2to1.6 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 0.40 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.050 | % | |
| MeltViscosity | 260°C,1500sec^-1 | ISO11443 | 210 | Pa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 43.0 | Mpa |
| Tensile modulus 2 | ASTMD638 | 1900 | Mpa | |
| Tensile modulus | ISO527-2/1 | 1900 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 43.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 44.0 | Mpa |
| Tensile strength 3 | Break | ASTMD638 | 35.0 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 37.0 | Mpa |
| Elongation rate 3 | Yield | ASTMD638 | 4.0 | % |
| Tensile strain | Yield | ISO527-2/50 | 4.0 | % |
| Elongation rate 4 | Break | ASTMD638 | 150 | % |
| Tensile strain | Break | ISO527-2/50 | 100 | % |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 1900 | Mpa |
| Bending modulus 5 | ISO178 | 1800 | Mpa | |
| Bending strength 5,6 | ISO178 | 64.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 9 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 95.0 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 60.0 | °C |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 60.0 | °C |
| Vicat softening temperature | ASTMD152510 | 117 | °C | |
| -- | ISO306/B50 | 117 | °C | |
| -- | ISO306/B120 | 120 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 1E-04 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| MD：23to60°C | ISO11359-2 | 1.3E-04 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1E-04 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 7 | 23°C | ISO179/1eA | 70 | kJ/m² |
| CharpyUnnotchImpactStrength7 | -30°C | ISO179/1eU | NoBreak | |
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 20 | kJ/m² |
| 23°C | ISO180/1A | 65 | kJ/m² | |
| UnnotchedIzodImpactStrength8 | -40°C | ISO180/1U | NoBreak | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 100 | J |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 100 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.