PC/PBT XENOY™ X2500UV-BK1D355BZDD SABIC INNOVATIVE US
133
- Unit Price:
- $3260 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact No fill
- Application Areas:Electronic and electrical Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 265°C/2.16kg | ASTMD1238 | 9.0 | g/10min |
| Melt volume flow rate | 265°C/1.2kg | ISO1133 | 4.00 | cm3/10min |
| Shrinkage rate | MD3 | 内部方法 | 0.50到0.80 | % |
| MD:3.20mm | 内部方法 | 0.50到0.80 | % | |
| TD3 | 内部方法 | 0.50到0.80 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.70 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.20 | % | |
| Shrinkage rate | MD2 | 内部方法 | 0.50到0.80 | % |
| TD2 | 内部方法 | 0.50到0.80 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | --3 | ASTMD638 | 2200 | Mpa |
| Tensile strength | Yield4 | ASTMD638 | 56.0 | Mpa |
| Break4 | ASTMD638 | 55.0 | Mpa | |
| elongation | Yield4 | ASTMD638 | 5.0 | % |
| Break4 | ASTMD638 | 80 | % | |
| Bending modulus | 50.0mmSpan5 | ASTMD790 | 2150 | Mpa |
| --6 | ISO178 | 2150 | Mpa | |
| bending strength | --6,7 | ISO178 | 80.0 | Mpa |
| Yield,50.0mmSpan5 | ASTMD790 | 79.0 | Mpa | |
| Tensile strength | Break5 | ASTMD638 | 55.0 | Mpa |
| Break | ISO527-2/50 | 56.0 | Mpa | |
| elongation | Yield | ASTMD638,ISO527-2/50 | 5.0 | % |
| Yield5 | ASTMD638 | 5.0 | % | |
| Break | ASTMD638 | 100 | % | |
| Break5 | ASTMD638 | 80 | % | |
| Break | ISO527-2/50 | 70 | % | |
| Bending modulus | -- | ASTMD790 | 2100 | Mpa |
| 50.0mmSpan6 | ASTMD790 | 2150 | Mpa | |
| --7 | ISO178 | 2150 | Mpa | |
| Tensile modulus | --4 | ASTMD638 | 2200 | Mpa |
| -- | ISO527-2/1 | 2200 | Mpa | |
| Tensile strength | Yield | ASTMD638 | 53.0 | Mpa |
| Yield5 | ASTMD638 | 56.0 | Mpa | |
| Yield | ISO527-2/50 | 57.0 | Mpa | |
| bending strength | -- | ASTMD790 | 79.0 | Mpa |
| --7,8 | ISO178 | 80.0 | Mpa | |
| Yield,50.0mmSpan6 | ASTMD790 | 79.0 | Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 20.0 | mg |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,64.0mmSpan11 | ISO75-2/Bf | 126 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 108 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan11 | ISO75-2/Af | 108 | °C | |
| Vicat softening temperature | -- | ASTMD152512,ISO306/B5012 | 135 | °C |
| -- | ISO306/A50 | 145 | °C | |
| -- | ISO306/B120 | 136 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 8E-05 | cm/cm/°C |
| MD:23to80°C | ISO11359-2 | 8.2E-05 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 8.5E-05 | cm/cm/°C | |
| TD:23to80°C | ISO11359-2 | 8.7E-05 | cm/cm/°C | |
| thermal conductivity | ISO8302 | 0.18 | W/m/K | |
| Hot deformation temperature | 1.8MPa,Unannealed,64.0mmSpan10 | ISO75-2/Af | 108 | °C |
| Vicat softening temperature | -- | ASTMD152511,ISO306/B5011 | 135 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed,64.0mmSpan10 | ISO75-2/Bf | 126 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 1MHz | IEC60250 | 0.020 | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+14 | ohms·cm | |
| Dielectric strength | 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm |
| Relative permittivity | 50Hz | IEC60250 | 3.30 | |
| 60Hz | IEC60250 | 3.30 | ||
| 1MHz | IEC60250 | 3.10 | ||
| Dissipation factor | 50Hz | IEC60250 | 2E-03 | |
| 60Hz | IEC60250 | 2E-03 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 8 | -30°C | ISO179/1eA | 30 | kJ/m² |
| 23°C | ISO179/1eA | 50 | kJ/m² | |
| Simple supported beam without notch impact strength 8 | -30°C | ISO179/1eU | 无断裂 | |
| Unscented Izod Impact Strength 9 | -30°C | ISO180/1U | 无断裂 | |
| Impact strength of simply supported beam gap 9 | -30°C | ISO179/1eA | 30 | kJ/m² |
| 23°C | ISO179/1eA | 50 | kJ/m² | |
| Simply supported beam without notch impact strength 9 | -30°C | ISO179/1eU | 无断裂 | |
| Unscented Izod Impact Strength 10 | -30°C | ISO180/1U | 无断裂 | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 60.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 95.0 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm,TestingbySABIC | UL94 | HB | |
| Burning wire flammability index | 2.7mm | IEC60695-2-12 | 750 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.