PC/PBT XENOY™ X4830 SABIC INNOVATIVE US
118
- Unit Price:
- $3507 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 53MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High impact resistance Dimensional stability
- Application Areas:Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 266°C/5.0kg | ASTMD1238 | 7.0 | g/10min |
| Melt volume flow rate | 265°C/5.0kg | ISO1133 | 6.00 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.70to0.90 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 0.42 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.14 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTMD638 | 3400 | Mpa | |
| Tensile modulus | ISO527-2/1 | 3200 | Mpa | |
| Tensile strength | Yield | ASTMD638 | 56.0 | Mpa |
| Tensile strain | Yield | ISO527-2/50 | 4.2 | % |
| elongation | Break3 | ASTMD638 | 150 | % |
| Break4 | ASTMD638 | 140 | % | |
| Tensile strain | Break | ISO527-2/5 | 120 | % |
| Break | ISO527-2/50 | 110 | % | |
| Bending modulus 5 | 50.0mmSpan | ASTMD790 | 3100 | Mpa |
| Bending modulus 6 | ISO178 | 2900 | Mpa | |
| Bending strength 6,7 | ISO178 | 90.0 | Mpa | |
| FlexuralStrength5 | Yield,50.0mmSpan | ASTMD790 | 96.0 | Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 30.0 | mg |
| Tensile strength | Yield | ASTMD638 | 60.0 | Mpa |
| Tensile stress | Yield | ISO527-2/5 | 55.0 | Mpa |
| Yield | ISO527-2/50 | 61.0 | Mpa | |
| Tensile strength | Break3 | ASTMD638 | 60.0 | Mpa |
| Break4 | ASTMD638 | 60.0 | Mpa | |
| Tensile stress | Break | ISO527-2/5 | 60.0 | Mpa |
| Break | ISO527-2/50 | 55.0 | Mpa | |
| elongation | Yield | ASTMD638 | 4.5 | % |
| Yield | ASTMD638 | 4.1 | % | |
| Tensile strain | Yield | ISO527-2/5 | 4.1 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 125 | °C |
| Hot deformation temperature 10 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 119 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 106 | °C |
| Hot deformation temperature 10 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 97.0 | °C |
| Vicat softening temperature | ASTMD152511 | 133 | °C | |
| -- | ISO306/B50 | 133 | °C | |
| -- | ISO306/B120 | 135 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 6E-05 | cm/cm/°C |
| MD：-30to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 8.2E-05 | cm/cm/°C | |
| TD：-30to80°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| thermal conductivity | ISO8302 | 0.20 | W/m/K |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 8 | -30°C | ISO179/1eA | 12 | kJ/m² |
| 23°C | ISO179/1eA | 40 | kJ/m² | |
| Simple supported beam without notch impact strength 8 | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength 9 | -30°C | ISO180/1A | 9.0 | kJ/m² |
| 0°C | ISO180/1A | 15 | kJ/m² | |
| 23°C | ISO180/1A | 45 | kJ/m² | |
| Unscented Izod Impact Strength 9 | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Dart impact equipped with measuring instruments | -20°C,TotalEnergy | ASTMD3763 | 70.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 70.0 | J | |
| Multi axis Instrumented Impact Energy | ISO6603-2 | 110 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 105 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.