PC/PBT XENOY™ 5720U-1001 SABIC INNOVATIVE US
250
Unit Price:$2956 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 113MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance Low temperature impact re
- Application Areas:Plastic bag Household daily necessiti Lighting applications
- Color:--
- Grade:Cold resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.080 | % |
| Saturation, 23°C | ISO 62 | 0.28 | % | |
| Specific volume | ASTM D792 | 0.850 | cm³/g | |
| Melt flow rate | 250°C/2.16 kg | ISO 1133 | 3.0 | g/10 min |
| 266°C/5.0 kg | ASTM D1238 | 20 | g/10 min | |
| 265°C/2.16 kg | ASTM D1238 | 6.0 | g/10 min | |
| 250°C/5.0 kg | ASTM D1238, ISO 1133 | 11 | g/10 min | |
| 250°C/2.16 kg | ASTM D1238 | 3.8 | g/10 min | |
| Molten Volume Flow Rate (MVR) | 265°C/5.0 kg | ISO 1133 | 18.0 | cm3/10min |
| 265°C/2.16 kg | ISO 1133 | 6.00 | cm3/10min | |
| 250°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min | |
| 250°C/2.16 kg | ISO 1133 | 3.00 | cm3/10min | |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 1.0 到 1.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | -- 9, 10 | ISO 178 | 71.0 | Mpa |
| Yield, 50.0 mm Span 8 | ASTM D790 | 70.0 | Mpa | |
| Break, 50.0 mm Span 8 | ASTM D790 | 69.0 | Mpa | |
| Tensile modulus | -- | ISO 527-2/1 | 1790 | Mpa |
| -- 4 | ASTM D638 | 1810 | Mpa | |
| -- 3 | 内部方法 | 1830 | Mpa | |
| -- 2 | ASTM D638 | 1830 | Mpa | |
| elongation | Yield 7 | ASTM D638 | 4.6 | % |
| Yield 6 | 内部方法 | 4.6 | % | |
| Yield 5 | ASTM D638 | 4.0 | % | |
| Yield | ISO 527-2/5 | 4.1 | % | |
| Yield | ISO 527-2/50 | 4.6 | % | |
| Break 7 | ASTM D638 | 120 | % | |
| Break 6 | 内部方法 | 110 | % | |
| Break 5 | ASTM D638 | 120 | % | |
| Break | ISO 527-2/5 | 110 | % | |
| Break | ISO 527-2/50 | 120 | % | |
| Bending modulus | 50.0 mm Span 8 | ASTM D790 | 1660 | Mpa |
| -- 9 | ISO 178 | 1860 | Mpa | |
| Tensile strength | Yield 5 | ASTM D638 | 47.0 | Mpa |
| Yield 6 | 内部方法 | 45.0 | Mpa | |
| Yield 7 | ASTM D638 | 44.0 | Mpa | |
| Yield | ISO 527-2/5 | 44.0 | Mpa | |
| Yield | ISO 527-2/50 | 47.0 | Mpa | |
| Break 7 | ASTM D638 | 50.0 | Mpa | |
| Break 6 | 内部方法 | 47.0 | Mpa | |
| Break 5 | ASTM D638 | 48.0 | Mpa | |
| Break | ISO 527-2/5, ISO 527-2/50 | 43.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ASTM D152513, ISO 306/B5013 | 119 | °C |
| -- | ISO 306/B120 | 122 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 95°C | ASTM E831 | 9.8E-5 | cm/cm/°C |
| Flow : -30 to 80°C | ISO 11359-2 | 9.8E-5 | cm/cm/°C | |
| Across Flow : -40 to 95°C | ASTM E831 | 1.0E-4 | cm/cm/°C | |
| Across Flow : -30 to 80°C | ISO 11359-2 | 1.0E-4 | cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 108 | °C |
| 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 117 | °C | |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 12 | ISO 75-2/Bf | 109 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 83.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 95.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 12 | ISO 75-2/Af | 87.0 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 4.0 到 6.0 | hr | ||
| Suggested injection volume | 50 到 80 | % | ||
| Temperature at the rear of the barrel | 245 到 265 | °C | ||
| Temperature in the middle of the barrel | 250 到 270 | °C | ||
| Temperature at the front of the material cylinder | 255 到 275 | °C | ||
| Spray nozzle temperature | 255 到 270 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 50 到 80 | rpm | ||
| Exhaust hole depth | 0.013 到 0.020 | mm | ||
| drying temperature | 110 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 260 到 275 | °C | ||
| Mold temperature | 65 到 90 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 11 | -30°C | ISO 179/1eA | 47 | kJ/m² |
| 23°C | ISO 179/1eA | 55 | kJ/m² | |
| Dart impact equipped with measuring instruments | -40°C, Energy at Peak | ASTM D3763 | 49.0 | J |
| -40°C, Total Energy | ASTM D3763 | 59.0 | J | |
| -30°C, Energy at Peak | ASTM D3763 | 49.0 | J | |
| -30°C, Total Energy | ASTM D3763 | 61.0 | J | |
| -20°C, Energy at Peak | ASTM D3763 | 41.0 | J | |
| -20°C, Total Energy | ASTM D3763 | 53.0 | J | |
| 23°C, Energy at Peak | ASTM D3763 | 44.0 | J | |
| 23°C, Total Energy | ASTM D3763 | 54.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.