| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Molten Volume Flow Rate (MVR) | 230°C/2.16 kg | ISO 1133 | 39.0 | cm3/10min |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.030 | % |
| Biomass content 3 | | CSA LISTED | 43 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO 527-2 | 85.0 | Mpa |
| Tensile stress | Break | ISO 527-2 | 15.0 | Mpa |
| Tensile stress | 5.0% Strain | ISO 527-2 | 4.80 | Mpa |
| Tensile stress | 10% Strain | ISO 527-2 | 7.70 | Mpa |
| Tensile stress | 50% Strain | ISO 527-2 | 10.8 | Mpa |
| Tensile stress | 100% Strain | ISO 527-2 | 10.8 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ISO 306/B50 | 38.0 | °C |
| Melting temperature 4 | | ISO 11357-3 | 180 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | IEC 60093 | > 1.0E+15 | ohms·cm |
| Dielectric strength | | IEC 60243-1 | 20 | KV/mm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | Shore D, 3 sec | ISO 868 | 45 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability level | 1.5 mm | IEC 60695-11-10, -20 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.