| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 10 | g/10min |
| Shrinkage rate | MD：2.00mm | ASTMD955 | 0.50 | % |
| Water absorption rate | Equilibrium,23°C,65%RH | ASTMD570 | 0.48 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | -- | ASTMD638 | 23.0 | Mpa |
| Tensile strength | 50%Strain | ASTMD638 | 6.40 | Mpa |
| elongation | Break | ASTMD638 | 690 | % |
| Bending modulus | | ASTMD790 | 51.0 | Mpa |
| compressive strength | 10%Strain | ASTMD695 | 4.60 | Mpa |
| Taber abraser | 1000Cycles | ASTMD1044 | 20.0 | mg |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | <25.0 | °C |
| Brittle temperature | | JISK6301 | <-65.0 | °C |
| Vicat softening temperature | | ASTMD1525 | 120 | °C |
| Melting temperature | | DSC | 172 | °C |
| Linear coefficient of thermal expansion | MD | ASTME831 | 1.7E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | ASTMD257 | 2E+12 | ohms·cm |
| Dielectric strength | | JISK2111 | 20 | KV/mm |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|
| Permanent compression deformation | | JISK6301 | 50 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | Shore A | JISK6301 | 89 | |
| Shore hardness | Shore D | ASTMD2240 | 38 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| Resilience | | JISK6301 | 78 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.