TPEE RITEFLEX® 672 CELANESE USA

109

Unit Price:
$3519 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High rigidity
Application Areas:High temperature hot plug Automotive components
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Specific volume		ASTMD792	0.802	cm³/g
Melt mass flow rate		ASTMD1238	10to15	g/10min
Melt mass flow rate	Melt mass flow rate		ISO1133	16	g/10min
Shrinkage rate	MD	ASTMD955	2.0	%
	Shrinkage rate	TD	ISO294-4	1.7to2.2	%
	Shrinkage rate	Shrinkage rate	MD	ISO294-4	1.7to2.2	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ASTMD638	635	Mpa
Tensile modulus	Tensile modulus		ISO527-2/1A/1	500	Mpa
Bending modulus	23°C	ISO178	450	Mpa
Bending stress	23°C	ISO178	22.0	Mpa
Tab	1000Cycles,CS-18Wheel	ASTMD4060	30.0	mg
RossFlex		内部方法	>1.0E+6	cycles
Tensile stress	Yield	ISO527-2/1A/50	28.0	Mpa
Tensile strength	Break,23°C	ASTMD638	29.2	Mpa
Tensile stress	Break	ISO527-2	40.0	Mpa
	Tensile stress	5.0%Strain	ISO527-2	21.0	Mpa
		Tensile stress	10%Strain	ISO527-2	27.0	Mpa
		Tensile stress	Tensile stress	50%Strain	ISO527-2	25.0	Mpa
Tensile strain	Yield	ISO527-2/1A/50	19	%
elongation	Break,23°C	ASTMD638	300	%
Nominal tensile fracture strain		ISO527-2/1A/50	>50	%
Bending modulus	-40°C	ISO178	2400	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature		ASTMD1525	204	°C
Peak melting temperature		ASTMD3418	214	°C
Melting temperature 5		ISO11357-3	215	°C
Linear coefficient of thermal expansion	MD	ASTMD696	1.7E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO11359-2	1.4E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	118	°C
Glass transition temperature		ASTMD3418	-23.3	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	2E+17	ohms
Dielectric strength		IEC60243-1	28	KV/mm
Relative permittivity	1MHz	IEC60250	3.70
Dissipation factor	1MHz	IEC60250	0.040
Leakage Trace Index		IEC60112	>600	V

elastomer	Test Condition	Test Method	Test Result	Unit
TearStrength-Flow3		ISO34-1	190	kN/m
Permanent compression deformation	23°C	ASTMD395	<1.0	%
Basho elasticity	--	内部方法	40	%
Basho elasticity	Basho elasticity	--	ASTMD2632	40	%

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Shore hardness	Shore D	ASTMD2240	72
Shore hardness	Shore hardness	Shore D,15sec	ISO868	72

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
tear strength		Kg/m	217.2	kN/m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.