TPEE RITEFLEX® 663 CELANESE USA

109

Unit Price:
$3314 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:UV resistance
Application Areas:High temperature hot plug Automotive components
Color:--
Grade:Extrusion grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD	ASTMD955	1.9	%
	Shrinkage rate	TD	ISO294-4	1.7to2.1	%
	Shrinkage rate	Shrinkage rate	MD	ISO294-4	1.7to2.0	%
Melt mass flow rate		ASTMD1238	16	g/10min
Melt mass flow rate	Melt mass flow rate	240°C/2.16kg	ISO1133	19	g/10min
Specific volume		ASTMD792	0.820	cm³/g

Mechanical performance	Test Condition	Test Method	Test Result	Unit
RossFlex		内部方法	>1.0E+6	cycles
Nominal tensile fracture strain		ISO527-2/1A/50	>50	%
Bending stress	23°C	ISO178	17.5	Mpa
Tensile strength	Break,23°C	ASTMD638	26.2	Mpa
Tensile stress	Break	ISO527-2/1A/50	38.0	Mpa
	Tensile stress	5.0%Strain	ISO527-2	13.0	Mpa
		Tensile stress	10%Strain	ISO527-2	18.0	Mpa
			Tensile stress	50%Strain	ISO527-2/1A/50	21.0	Mpa
			Tensile stress	Tensile stress	Yield	ISO527-2/1A/50	22.0	Mpa
Tensile strain	Yield	ISO527-2/1A/50	44	%
Tensile modulus	23°C	ASTMD638	365	Mpa
Tensile modulus	Tensile modulus		ISO527-2/1A/1	350	Mpa
elongation	Break,23°C	ASTMD638	320	%
Bending modulus	-40°C	ISO178	1900	Mpa
Bending modulus	Bending modulus	23°C	ISO178	325	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	114	°C
Vicat softening temperature		ASTMD1525	195	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	1.8E-04	cm/cm/°C
Glass transition temperature		ASTMD3418	-42.8	°C
Melting temperature 5		ISO11357-3	212	°C
Peak melting temperature		ASTMD3418	210	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength 4		ASTMD149	13	KV/mm
Relative permittivity	1MHz	IEC60250	4.00
Leakage Trace Index		ASTMD3638	>600	V
Leakage Trace Index	Leakage Trace Index		IEC60112	>600	V
Dissipation factor	1MHz	IEC60250	0.040
Dielectric strength		IEC60243-1	14	KV/mm
Surface resistivity		IEC60093	1E+16	ohms
Volume resistivity		ASTMD257	2E+13	ohms·cm
Volume resistivity	Volume resistivity		IEC60093	2E+15	ohms·cm

elastomer	Test Condition	Test Method	Test Result	Unit
Permanent compression deformation	23°C	ASTMD395	<1.0	%
Basho elasticity	--	内部方法	40	%
Basho elasticity	Basho elasticity	--	ASTMD2632	40	%
TearStrength-Flow2		ISO34-1	160	kN/m

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Shore hardness	Shore D	ASTMD2240	63
Shore hardness	Shore hardness	Shore D,15sec	ISO868	63

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
tear strength		Kg/m	269.7	kN/m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.