TPEE RITEFLEX® 655 CELANESE USA

115

Unit Price:
$3641 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
45MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:UV resistance
Application Areas:High temperature hot plug Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Specific volume		ASTMD792	0.842	cm³/g
Melt mass flow rate		ASTMD1238	7.0to11	g/10min
Melt mass flow rate	Melt mass flow rate	220°C/2.16kg	ISO1133	10	g/10min
Shrinkage rate	MD	ASTMD955	1.5	%
	Shrinkage rate	TD	ISO294-4	1.7to2.1	%
	Shrinkage rate	Shrinkage rate	MD	ISO294-4	1.6to1.9	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ASTMD638	241	Mpa
Tensile modulus	Tensile modulus		ISO527-2/1A/1	175	Mpa
Tensile stress	Yield	ISO527-2/1A/50	15.0	Mpa
Tensile strength	Break,23°C	ASTMD638	25.2	Mpa
Tensile stress	Break	ISO527-2/1A/50	30.0	Mpa
	Tensile stress	5.0%Strain	ISO527-2	8.00	Mpa
		Tensile stress	10%Strain	ISO527-2	12.0	Mpa
		Tensile stress	Tensile stress	50%Strain	ISO527-2/1A/50	15.0	Mpa
Tensile strain	Yield	ISO527-2/1A/50	28	%
elongation	Break,23°C	ASTMD638	430	%
Tensile strain	Break	ISO527-2/1A/50	>300	%
Bending modulus	-40°C	ISO178	700	Mpa
	Bending modulus	23°C	ISO178	175	Mpa
	Bending modulus	Bending modulus	100°C	ISO178	86.0	Mpa
Bending stress	3.5%Strain	ISO178	7.00	Mpa
Bending stress	Bending stress	23°C	ISO178	10.0	Mpa
RossFlex		内部方法	>1.0E+6	cycles

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	75.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	48.0	°C
Glass transition temperature		ASTMD3418	-56.7	°C
Vicat softening temperature		ASTMD1525	181	°C
Peak melting temperature		ASTMD3418	200	°C
Melting temperature 5		ISO11357-3	200	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	1.7E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	4E+15	ohms
Volume resistivity		ASTMD257	5E+12	ohms·cm
Volume resistivity	Volume resistivity		IEC60093	4E+12	ohms·cm
Dielectric strength 4		ASTMD149	14	KV/mm
Dielectric strength		IEC60243-1	14	KV/mm
Relative permittivity	1MHz	IEC60250	4.40
Dissipation factor	1MHz	IEC60250	0.040
Leakage Trace Index		ASTMD3638	>600	V
Leakage Trace Index	Leakage Trace Index		IEC60112	>600	V

elastomer	Test Condition	Test Method	Test Result	Unit
Basho elasticity	--	内部方法	48	%
Basho elasticity	Basho elasticity	--	ASTMD2632	48	%
TearStrength-Flow2		ISO34-1	120	kN/m
Permanent compression deformation	23°C	ASTMD395	<1.0	%

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Shore hardness	Shore D	ASTMD2240	55
Shore hardness	Shore hardness	Shore D,15sec	ISO868	55

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
tear strength		Kg/m	217.2	kN/m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.