TPEE RITEFLEX® 640 CELANESE USA

124

Unit Price:
$3987 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
31MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:UV resistance
Application Areas:High temperature hot plug Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Specific volume		ASTMD792	0.882	cm³/g
Melt mass flow rate		ASTMD1238	8.0to12	g/10min
Melt mass flow rate	Melt mass flow rate	220°C/2.16kg	ISO1133	10	g/10min
Shrinkage rate	MD	ASTMD955	1.0	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	1.2to1.4	%
Shear		内部方法	1000	1/°C
viscosity		内部方法	351	Pa·s

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ASTMD638	92.4	Mpa
Tensile modulus	Tensile modulus		ISO527-2/1A/1	75.0	Mpa
Tensile strength	Break,23°C	ASTMD638	20.7	Mpa
Tensile stress	Break	ISO527-2/1A/50	17.0	Mpa
	Tensile stress	5.0%Strain	ISO527-2	3.00	Mpa
		Tensile stress	10%Strain	ISO527-2	5.00	Mpa
		Tensile stress	Tensile stress	50%Strain	ISO527-2/1A/50	8.00	Mpa
elongation	Break,23°C	ASTMD638	480	%
Tensile strain	Break	ISO527-2/1A/50	>300	%
Bending modulus	-40°C	ISO178	115	Mpa
Bending modulus	Bending modulus	23°C	ISO178	70.0	Mpa
Bending stress	3.5%Strain	ISO178	3.00	Mpa
Bending stress	Bending stress	23°C	ISO178	5.00	Mpa
Tab	1000Cycles,CS-18Wheel	ASTMD4060	90.0	mg
RossFlex		内部方法	>1.0E+6	cycles

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature		ASTMD1525	136	°C
Peak melting temperature		ASTMD3418	180	°C
Melting temperature 5		ISO11357-3	170	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	2.2E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	56.0	°C
Brittle temperature		ISO974	-78.0	°C
Glass transition temperature		ASTMD3418	-65.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	3E+15	ohms
Volume resistivity		ASTMD257	5E+12	ohms·cm
Volume resistivity	Volume resistivity		IEC60093	5E+12	ohms·cm
Dielectric strength 4		ASTMD149	12	KV/mm
Dielectric strength		IEC60243-1	13	KV/mm
Relative permittivity	1MHz	IEC60250	4.70
Dissipation factor	1MHz	IEC60250	0.030
Leakage Trace Index		ASTMD3638	>600	V
Leakage Trace Index	Leakage Trace Index		IEC60112	>600	V

elastomer	Test Condition	Test Method	Test Result	Unit
TearStrength-Flow2		ISO34-1	84	kN/m
Basho elasticity		ASTMD2632	59	%

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak
Unscented Izod impact strength	-30°C	ISO180/1U	NoBreak
Unscented Izod impact strength	Unscented Izod impact strength	23°C	ISO180/1U	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Shore hardness	Shore D	ASTMD2240	40
Shore hardness	Shore hardness	Shore D,15sec	ISO868	40
Durometer		内部方法	40.0

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB

Supplementary Information	Test Condition	Test Method	Test Result	Unit
tear strength		Kg/m	110.3	kN/m
Temperature		内部方法	220	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.