PPA Zytel® HTN42G30EF NC010 DUPONT JAPAN
139
- Unit Price:
- $5796 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 40MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Glass fiber reinforced
- Application Areas:Electronic and Electrical
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 0.90 | % |
| 流量 | ISO 294-4 | 0.40 | % | |
| Biobased Carbon Content | ISO 16620-2 | 21 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2 | 11700 | Mpa | |
| Bending modulus | ISO 178 | 11300 | Mpa | |
| Bending stress | ISO 178 | 210 | Mpa | |
| Tensile stress | Break | ISO 527-2 | 134 | Mpa |
| Tensile strain | Break | ISO 527-2 | 1.7 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 2.0E-5 | cm/cm/°C |
| Flow : -40 to 23°C | ISO 11359-2 | 1.7E-5 | cm/cm/°C | |
| Flow : 55 to 160°C | ISO 11359-2 | 2.0E-5 | cm/cm/°C | |
| Across Flow | ISO 11359-2 | 5.1E-5 | cm/cm/°C | |
| Across Flow : -40 to 23°C | ISO 11359-2 | 4.3E-5 | cm/cm/°C | |
| Across Flow : 55 to 160°C | ISO 11359-2 | 8.4E-5 | cm/cm/°C | |
| Melting temperature 2 | ISO 11357-3 | 314 | °C | |
| RTI | 0.40 mm | UL 746 | 125 | °C |
| 3.0 mm | UL 746 | 130 | °C | |
| RTI Imp | 0.40 mm | UL 746 | 115 | °C |
| 3.0 mm | UL 746 | 120 | °C | |
| RTI Elec | 0.40 mm | UL 746 | 130 | °C |
| 3.0 mm | UL 746 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | IEC 60243-1 | 33 | KV/mm | |
| Leakage Trace Index | IEC 60112 | 600 | V | |
| Volume resistivity | IEC 62631-3-1 | 1.0E+16 | ohms·m |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 100 | °C | ||
| Drying time - hot air dryer | 6.0 到 8.0 | hr | ||
| Suggested maximum moisture content | 0.10 | % | ||
| Processing (melt) temperature | 325 到 335 | °C | ||
| Mold temperature | 110 到 130 | °C | ||
| Drying Recommended | yes |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 35 | kJ/m² |
| 23°C | ISO 179/1eU | 35 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 0.40 mm | IEC 60695-2-12 | 960 | °C |
| 1.5 mm | IEC 60695-2-12 | 960 | °C | |
| 3.0 mm | IEC 60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 0.40 mm | IEC 60695-2-13 | 750 | °C |
| 1.5 mm | IEC 60695-2-13 | 800 | °C | |
| 3.0 mm | IEC 60695-2-13 | 825 | °C | |
| UL flame retardant rating | 0.40 mm | UL 94, IEC 60695-11-10, -20 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.