PPA AKROLOY® PA GF 50 BK AKRO-PLASTIC GERMANY
179
- Unit Price:
- $4392 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Molten Volume Flow Rate (MVR) | 275°C/5.0 kg | ISO 1133 | 9.00 | cm3/10min |
| Spiral Flow 1, 2 | 内部方法 | 54.0 | CM | |
| Shrinkage rate | Across Flow | ISO 294-4 | 0.50 | % |
| 流量 | ISO 294-4 | 0.50 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 3.5 到 4.0 | % |
| Humidity Absorption - 62% RH | 70°C | ISO 1110 | 1.1 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 17500 | Mpa | |
| Tensile stress | Break | ISO 527-2/5 | 250 | Mpa |
| Tensile strain | Break | ISO 527-2/5 | 3.0 | % |
| Bending modulus 3 | ISO 178 | 16400 | Mpa | |
| Bending stress 3 | ISO 178 | 380 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 245 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 225 | °C | |
| Vicat softening temperature | ISO 306/B50 | 242 | °C | |
| Melting temperature 4 | DIN EN 11357-1 | 255 | °C | |
| Linear coefficient of thermal expansion | Flow : 23 to 80°C | ISO 11359-2 | 1.5E-5 | cm/cm/°C |
| Across Flow : 23 to 80°C | ISO 11359-2 | 6.5E-5 | cm/cm/°C | |
| 50% Loss of Tensile Strength, 20000 hr | 110 到 130 | °C | ||
| 50% Loss of Tensile Strength, 5000 hr | 140 到 150 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 1.5E+17 | ohms | |
| Relative permittivity | 1 MHz | IEC 60250 | 4.42 | |
| Leakage Trace Index | Solution A | IEC 60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 95 | kJ/m² |
| 23°C | ISO 179/1eU | 110 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H 961/30 | ISO 2039-1 | 290 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate | 1.00 mm | FMVSS 302 | < 100 | mm/min |
| UL flame retardant rating | 0.8 mm | UL 94 | HB | |
| Burning wire flammability index | 1.6 mm | IEC 60695-2-12 | 700 | °C |
| Reinforcement Content | ISO 1172 | 50 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.