PPA AMODEL® A-6135 HN BK324 SOLVAY USA

148

Unit Price:
$5604 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
23MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Chemical resistance Low moisture absorption
Application Areas:Vehicle electronics Shell
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD	ASTMD955	0.60	%
	Shrinkage rate	TD	ASTMD955	0.90	%
		Shrinkage rate	TD	ISO294-4	1.0	%
		Shrinkage rate	Shrinkage rate	MD	ISO294-4	0.50	%
Water absorption rate	24hr	ASTMD570	0.30	%
Water absorption rate	Water absorption rate	23°C,24hr	ISO62	0.29	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ASTMD638	13800	Mpa
	Tensile modulus	23°C	ISO527-2	11500	Mpa
		Tensile modulus	100°C	ISO527-2	7310	Mpa
			Tensile modulus	150°C	ISO527-2	6270	Mpa
			Tensile modulus	Tensile modulus	175°C	ISO527-2	5310	Mpa
Tensile strength		ASTMD638	203	Mpa
Tensile stress	Break,23°C	ISO527-2	211	Mpa
	Tensile stress	Break,24°C	ISO527-2	121	Mpa
		Tensile stress	Break,150°C	ISO527-2	92.4	Mpa
		Tensile stress	Tensile stress	Break,175°C	ISO527-2	82.0	Mpa
elongation	Break	ASTMD638	1.9	%
Tensile strain	Break,23°C	ISO527-2	2.0	%
Tensile strain	Tensile strain	Break,24°C	ISO527-2	4.3	%
Bending stress	3.5%Strain,150°C	ISO178	123	Mpa
Bending stress	Bending stress	3.5%Strain,175°C	ISO178	112	Mpa
compressive strength		ASTMD695	148	Mpa
shear strength		ASTMD732	87.6	Mpa
Poisson's ratio		7.58	0.39
Tensile strain	Break,150°C	ISO527-2	4.9	%
Tensile strain	Tensile strain	Break,175°C	ISO527-2	4.7	%
Bending modulus		ASTMD790	11400	Mpa
	Bending modulus	23°C	ISO178	11400	Mpa
		Bending modulus	100°C	ISO178	6600	Mpa
			Bending modulus	150°C	ISO178	4900	Mpa
			Bending modulus	Bending modulus	175°C	ISO178	4600	Mpa
bending strength		ASTMD790	310	Mpa
Bending stress	3.5%Strain,23°C	ISO178	300	Mpa
Bending stress	Bending stress	3.5%Strain,100°C	ISO178	170	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion	TD：100to200°C	ASTME831	1E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	303	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	288	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,3.20mm	ASTMD648	291	°C
Melting temperature		ISO11357-3	310	°C
Melting temperature	Melting temperature		ASTMD570	310	°C
Linear coefficient of thermal expansion	MD：0to100°C	ASTME831	2.2E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：100to200°C	ASTME831	1.6E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：0to100°C	ASTME831	6.1E-05	cm/cm/°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179/1eU	60	kJ/m²
Unscented Izod impact strength	23°C	ISO180	62	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTMD785	125

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.