PETG 0601 EASTMAN USA
222
- Unit Price:
- $2477 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 285MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High transparency High toughness
- Application Areas:packing sporting goods
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23°C,24hr | ASTMD570,ISO62 | 0.13 | % |
| Intrinsic viscosity 2 | Film:23°C | 内部方法 | 0.70 | |
| Pellets:23°C | 内部方法 | 0.75 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | 23°C | ISO178 | 68.0 | Mpa |
| Yield,23°C | ASTMD790 | 70.0 | Mpa | |
| Tear resistance | M.D.:23°C | 93 | N | |
| T.D.:23°C | 93 | N | ||
| Tensile modulus | 23°C | ASTMD638,ISO527-2 | 2100 | Mpa |
| Tensile strength | Yield,23°C | ASTMD638,ISO527-2 | 50.0 | Mpa |
| Break,23°C | ASTMD638,ISO527-2 | 28.0 | Mpa | |
| elongation | Break,23°C | ASTMD638 | 130 | % |
| Break,23°C | ISO527-2 | 100 | % | |
| Bending modulus | 23°C | ASTMD790 | 2100 | Mpa |
| 23°C | ISO178 | 2000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 70.0 | °C |
| 1.8MPa,Unannealed | ASTMD648 | 64.0 | °C | |
| Glass transition temperature | DSC | 80.0 | °C | |
| Vicat softening temperature | ASTMD1525 | 85.0 | °C | |
| Linear coefficient of thermal expansion | MD：-30to40°C | ASTMD696 | 5.1E-05 | cm/cm/°C |
| specific heat | 60°C | DSC | 1300 | J/kg/°C |
| 100°C | DSC | 1760 | J/kg/°C | |
| 150°C | DSC | 1880 | J/kg/°C | |
| 200°C | DSC | 1970 | J/kg/°C | |
| 250°C | DSC | 2050 | J/kg/°C | |
| thermal conductivity | 23°C | ASTMC177 | 0.21 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 1E+16 | ohms | |
| Volume resistivity | 23°C | ASTMD257 | 1E+15 | ohms·cm |
| Dielectric strength 10 | 23°C | ASTMD149 | 16 | KV/mm |
| Dielectric constant | 23°C,1kHz | ASTMD150 | 2.60 | |
| 23°C,1MHz | ASTMD150 | 2.40 | ||
| Dissipation factor | 23°C,1kHz | ASTMD150 | 5E-03 | |
| 23°C,1MHz | ASTMD150 | 0.020 | ||
| Arc resistance | ASTMD495 | 158 | sec |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film thickness - tested | 250 | µm | ||
| Secant modulus | MD | ASTMD882 | 1900 | Mpa |
| TD | ASTMD882 | 1900 | Mpa | |
| Tensile strength | MD:Yield | ASTMD882 | 52.0 | Mpa |
| TD:Yield | ASTMD882 | 52.0 | Mpa | |
| MD:Break | ASTMD882 | 59.0 | Mpa | |
| Tear resistance of pants 4 | TD | ISO6383-1 | 36.0 | N/mm |
| Oxygen permeability rate | 23°C | ASTMD3985 | 10 | cm³·mm/m²/atm/24hr |
| Water vapor permeability | 38°C,100%RH | ASTMF1249 | 7.0 | g/m²/24hr |
| CarbonDioxidePermeability5 | 23°C | ASTMD1434 | 49 | cm³·mm/m²/atm/24hr |
| Resistance to tear propagation 6 | M.D.:23°C | ASTMD1938 | 36 | kN/m |
| T.D.:23°C | ASTMD1938 | 36 | kN/m | |
| Tensile strength | TD:Break | ASTMD882 | 55.0 | Mpa |
| elongation | MD:Yield | ASTMD882 | 4.0 | % |
| TD:Yield | ASTMD882 | 4.0 | % | |
| MD:Break | ASTMD882 | 400 | % | |
| TD:Break | ASTMD882 | 400 | % | |
| Falling hammer impact 3 | -18°C | ASTMD1709A | 500 | g |
| 23°C | ASTMD1709A | 400 | g | |
| Elmondov tear strength | MD | ASTMD1922 | 1400 | g |
| TD | ASTMD1922 | 1700 | g | |
| Tear resistance of pants 4 | MD | ISO6383-1 | 36.0 | N/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam without notch impact strength | -40°C,3.20mm | ASTMD4812 | 无断裂 | |
| -30°C,3.20mm | ASTMD4812 | 无断裂 | ||
| -20°C,3.20mm | ASTMD4812 | 无断裂 | ||
| 23°C,3.20mm | ASTMD4812 | 无断裂 | ||
| -40°C7 | ISO180/1U | 无断裂 | ||
| -30°C7 | ISO180/1U | 无断裂 | ||
| -20°C7 | ISO180/1U | 无断裂 | ||
| 23°C7 | ISO180/1U | 无断裂 | ||
| Dart impact equipped with measuring instruments | -40°C,2.50mm,EnergyatPeakLoad | ASTMD3763 | 41.0 | J |
| -40°C,3.20mm,EnergyatPeakLoad | ASTMD3763 | 50.0 | J | |
| 23°C,2.50mm,EnergyatPeakLoad | ASTMD3763 | 28.0 | J | |
| 23°C,3.20mm,EnergyatPeakLoad | ASTMD3763 | 33.0 | J | |
| -40°C,2.50mm,能量to力量峰值8,9 | ISO6603-2 | 35.0 | J | |
| -40°C,3.20mm,能量to力量峰值8,9 | ISO6603-2 | 36.0 | J | |
| 23°C,2.50mm,能量to力量峰值8,9 | ISO6603-2 | 40.0 | J | |
| 23°C,3.20mm,能量to力量峰值8,9 | ISO6603-2 | 44.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale,23°C | ASTMD785 | 106 | |
| R-Sale,23°C | ISO2039-2 | 109 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| gloss | 45° | ASTMD2457 | 108 | |
| transmissivity | 常规 | ASTMD1003 | 89.0 | % |
| Total | ASTMD1003 | 91.0 | % | |
| transparency | ASTMD1746 | 85.0 | ||
| Haze | ASTMD1003 | 0.80 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.