Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | Flow | | 0.50 | % |
| Shrinkage rate | Across Flow | | 1.0 | % |
| Water absorption rate | Equilibrium | ASTM D570 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | | ASTM D638 | 150 | Mpa |
| elongation | Break | ASTM D638 | 3.1 | % |
| Bending modulus | | ASTM D790 | 11200 | Mpa |
| bending strength | | ASTM D790 | 238 | Mpa |
| friction coefficient | 与钢 - 动态 | | 0.14 | |
| Wear amount | -- 3 | | 1.80 | 10^-3 mm³/N·km |
| Wear amount | of counterpart 4 | | 0.00 | 10^-3 mm³/N·km |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion - flow | | ASTM D696 | 2.3E-5 | cm/cm/°C |
| Heat Distortion | | ASTM D648 | 200 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Processing (melt) temperature | | | 260 到 280 | °C |
| Mold temperature | | | 120 到 150 | °C |
| Injection pressure | | | 40.0 到 60.0 | Mpa |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 95 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.