PA9T Genestar™ G1350H KURARAY JAPAN
264
Unit Price:$11553 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced
- Application Areas:Electrical field Electronic field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 流动 : 1.00 mm | 0.20 | % | |
| 横向流动 : 1.00 mm | 0.80 | % | ||
| 吸水率 | 平衡, 40°C, 95%RH | 1.4 | % | |
| 熔流率（熔体流动速率） | 320°C/2.16 kg | ASTM D1238 | 42 | g/10 min |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 伸长率 | 断裂 | ASTM D638 | 4.0 | % |
| 弯曲模量 | ASTM D790 | 10000 | Mpa | |
| 弯曲强度 | ASTM D790 | 230 | Mpa | |
| 抗张强度 | ASTM D638 | 180 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 载荷下热变形温度 | 1.8 MPa, 未退火 | ASTM D648 | 290 | °C |
| 熔融温度 | 306 | °C | ||
| 玻璃转化温度 | 125 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 介电强度 | ASTM D149 | 30 | KV/mm | |
| 相比耐漏电起痕指数(CTI) | UL 746 | PLC 0 | ||
| 介电常数 | 10.0 GHz | ASTM D150 | 3.40 | |
| 体积电阻率 | ASTM D257 | 1.0E+16 | ohms·cm | |
| 耗散因数 | 10.0 GHz | ASTM D150 | 9.0E-3 |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bar Flow Length | 320°C, 500.0 µm | 5.30 | CM | |
| Weld Elongation | ASTM D638 | 0.60 | % | |
| Weld Strength | ASTM D638 | 45.0 | Mpa | |
| UL 阻燃等级 | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.