TPV Santoprene™ 8201-70 CELANESE USA
116
- Unit Price:
- $4644 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 16MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low friction coefficient Low mold expansion Recyclable materials Controllable mold expansi Cleanable Good melt strength Good colorability Ozone resistance Chemical resistance Low water absorption Not absorbing water
- Application Areas:Kitchen utensils Home appliance components Fatigue relief supplies Soft handle Stationery Smart phone
- Color:--
- Grade:Weather resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| -- | ASTMD792 | 0.948 | g/cm³ | |
| ISO1183 | 0.950 | g/cm³ |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTI | 1.10mm | UL746 | 90.0 | °C |
| 1.60mm | UL746 | 90.0 | °C | |
| 3.00mm | UL746 | 95.0 | °C | |
| Brittle temperature | ASTMD746,ISO812 | -63.0 | °C | |
| RTIElec | UL746 | 100 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| Hot wire ignition (HWI) | 1.60mm | UL746 | PLC3 | |
| 3.00mm | UL746 | PLC2 | ||
| High voltage arc ignition resistance index | PLC | UL746 | PLC5 |
| ageing | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| The rate of change in hardness of an air hardness tester | 支撐A,150°C,168hr | ASTMD573,ISO188 | 2.0 | |
| Change rate of ultimate elongation in air | 150°C,168hr | ASTMD573,ISO188 | -8.0 | % |
| Change rate of ultimate elongation | 23°C,168hr,在15％氯化钠中 | ASTMD471,ISO1817 | -2.0 | % |
| 23°C,168hr,在50%氢氧化钠中 | ASTMD471,ISO1817 | 2.0 | % | |
| 23°C,168hr,在98％硫酸中 | ASTMD471,ISO1817 | 4.0 | % | |
| 23°C,168hr,在IRM903油中 | ASTMD471,ISO1817 | -14 | % | |
| 23°C,168hr,在水中 | ASTMD471,ISO1817 | 8.0 | % | |
| Changes in air quality | 150°C,168hr | ASTMD573 | -9.0 | % |
| 150°C,168hr | ISO188 | -9.0 | % | |
| Change rate of tensile strength | 23°C,168hr,在IRM903油中 | ASTMD471,ISO1817 | -14 | % |
| 23°C,168hr,在水中 | ASTMD471,ISO1817 | -6.0 | % | |
| 23°C,168hr,在15％氯化钠中 | ASTMD471,ISO1817 | -1.0 | % | |
| 23°C,168hr,在50%氢氧化钠中 | ASTMD471,ISO1817 | -1.0 | % | |
| 23°C,168hr,在98％硫酸中 | ASTMD471,ISO1817 | 3.0 | % | |
| Change rate of tensile strength in air | 150°C,168hr | ASTMD573,ISO188 | -9.0 | % |
| Quality change rate | 23°C,168hr,在水中 | ASTMD471 | 0.0 | % |
| 23.0°C,168hr,在50%氢氧化钠中 | ISO1817 | 0.0 | % | |
| 23.0°C,168hr,在水中 | ISO1817 | 0.0 | % | |
| 23.0°C,168hr,在15％氯化钠中 | ISO1817 | 0.0 | % | |
| 23.0°C,168hr,在98％硫酸中 | ISO1817 | 1.0 | % | |
| 23.0°C,168hr,在IRM903油中 | ISO1817 | 48 | % | |
| 23°C,168hr,在15％氯化钠中 | ASTMD471 | 0.0 | % | |
| 23°C,168hr,在50%氢氧化钠中 | ASTMD471 | 0.0 | % | |
| 23°C,168hr,在98％硫酸中 | ASTMD471 | 1.0 | % | |
| 23°C,168hr,在IRM903油中 | ASTMD471 | 48 | % | |
| Support A, 23 ° C, 168hr, in 15% sodium chloride | ASTMD471 | 1.0 | ||
| ISO1817 | 1.0 | |||
| Support A, 23 ° C, 168hr, in 50% sodium hydroxide | ISO1817 | 1.0 | ||
| ASTMD471 | 1.0 | |||
| Support A, 23 ° C, 168hr, in 98% sulfuric acid | ASTMD471 | -1.0 | ||
| ISO1817 | -1.0 | |||
| Support A, 23 ° C, 168hr, in IRM903 oil | ISO1817 | -14 | ||
| ASTMD471 | -14 | |||
| Support A, 23 ° C, 168hr, in water | ASTMD471,ISO1817 | -1.0 |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23°C1 | ASTMD624 | 26.0 | kN/m | |
| 23°C2 | ISO34-1 | 26 | kN/m | |
| 70°C,22hr3 | ASTMD395B | 36 | % | |
| 125°C,70hr4 | ASTMD395B | 57 | % | |
| Tensile stress transverse flow rate | 100%Strain,23°C | ASTMD412,ISO37 | 2.90 | Mpa |
| Tensile strength - transverse flow rate | Break,23°C | ASTMD412,ISO37 | 7.50 | Mpa |
| Elongation rate - lateral flow rate | Break,23°C | ASTMD412,ISO37 | 570 | % |
| 70°C,22hr5 | ISO815 | 36 | % | |
| 125°C,70hr6 | ISO815 | 57 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore A,15sec,23°C,2.00mm | ISO868 | 75 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.10mm | UL94 | HB | |
| 1.60mm | UL94 | HB | ||
| 3.00mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.