TPV Santoprene™ 8201-60 CELANESE USA
111
- Unit Price:
- $4604 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low friction coefficient Low mold expansion Recyclable materials Controllable mold expansi Cleanable Good melt strength Good colorability Ozone resistance Chemical resistance Low water absorption Not absorbing water
- Application Areas:Kitchen utensils Home appliance components Fatigue relief supplies Soft handle Stationery Smart phone Kitchen utensils Home appliance components Fatigue relief supplies Soft handle Phone Stationery
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Brittle temperature | ASTMD746 | -60.0 | °C | |
| ISO812 | -60.0 | °C | ||
| RTIElec | UL746 | 100 | °C | |
| RTIStr | 1.1mm | UL746 | 90.0 | °C |
| 1.6mm | UL746 | 90.0 | °C | |
| 3.0mm | UL746 | 95.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 | |
| Hot wire ignition (HWI) | 1.6mm | UL746 | PLC3 | |
| 3.0mm | UL746 | PLC2 | ||
| High arc combustion index | HAI | UL746 | PLC0 | |
| High voltage arc ignition resistance index | PLC | UL746 | PLC5 |
| ageing | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ChangeinDurometerHardnessAir | ShoreA,150°C,168hr | ASTMD573 | 1.0 | |
| ChangeinShoreHardnessinAir | ShoreA,150°C,168hr | ISO188 | 1.0 | |
| ChangeinMassinAir | 150°C,168hr | ASTMD573 | -8.0 | % |
| 150°C,168hr | ISO188 | -8.0 | % | |
| Changes in tensile stress during fracture | 23°C,168hr,inIRM903Oil | ISO1817 | -21 | % |
| 23°C,168hr,inSodiumChloride,15% | ISO1817 | -5.0 | % | |
| 23°C,168hr,inSodiumHydroxide,50% | ISO1817 | -2.0 | % | |
| 23°C,168hr,inSulfuricAcid,98% | ISO1817 | 5.0 | % | |
| 23°C,168hr,在水中 | ISO1817 | 11 | % | |
| Change rate of ultimate elongation in air | 150°C,168hr | ASTMD573 | -7.0 | % |
| Change rate of hardness of hardness tester 2 | ShoreA,23°C,168hr,inIRM903Oil | ASTMD471 | -13 | |
| ShoreA,23°C,168hr,inSodiumChloride,15% | ASTMD471 | 2.0 | ||
| ShoreA,23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | 2.0 | ||
| ShoreA,23°C,168hr,inSulfuricAcid,98% | ASTMD471 | -1.0 | ||
| ShoreA,23°C,168hr,inWater | ASTMD471 | 0.0 | ||
| ChangeinShoreHardness | ShoreA,23°C,168hr,inIRM903Oil | ISO1817 | -13 | |
| ShoreA,23°C,168hr,inSodiumChloride,15% | ISO1817 | 2.0 | ||
| ShoreA,23°C,168hr,inSodiumHydroxide,50% | ISO1817 | 2.0 | ||
| ShoreA,23°C,168hr,inSulfuricAcid,98% | ISO1817 | -1.0 | ||
| ShoreA,23°C,168hr,inWater | ISO1817 | 0.0 | ||
| Change rate of ultimate elongation | 23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | -2.0 | % |
| 23°C,168hr,inSulfuricAcid,98% | ASTMD471 | 5.0 | % | |
| 23°C,168hr,在水中 | ASTMD471 | 11 | % | |
| 23°C,168hr,inIRM903Oil | ASTMD471 | -21 | % | |
| 23°C,168hr,inSodiumChloride,15% | ASTMD471 | -5.0 | % | |
| Change rate of tensile strength | 23°C,168hr,inIRM903Oil | ASTMD471 | -17 | % |
| 23°C,168hr,inSodiumChloride,15% | ASTMD471 | -4.0 | % | |
| 23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | -2.0 | % | |
| 23°C,168hr,inSulfuricAcid,98% | ASTMD471 | 3.0 | % | |
| 23°C,168hr,在水中 | ASTMD471 | -3.0 | % | |
| 23°C,168hr,inIRM903Oil | ISO1817 | -17 | % | |
| 23°C,168hr,inSodiumChloride,15% | ISO1817 | -4.0 | % | |
| 23°C,168hr,inSodiumHydroxide,50% | ISO1817 | -2.0 | % | |
| 23°C,168hr,inSulfuricAcid,98% | ISO1817 | 3.0 | % | |
| 23°C,168hr,在水中 | ISO1817 | -3.0 | % | |
| Change rate of tensile strength in air | 150°C,168hr | ASTMD573 | -9.0 | % |
| 150°C,168hr | ISO188 | -9.0 | % | |
| Quality change rate | 23°C,168hr,inIRM903Oil | ASTMD471 | 47 | % |
| 23°C,168hr,inSodiumChloride,15% | ASTMD471 | 0.0 | % | |
| 23°C,168hr,inSodiumHydroxide,50% | ASTMD471 | 0.0 | % | |
| 23°C,168hr,inSulfuricAcid,98% | ASTMD471 | 0.0 | % | |
| 23°C,168hr,在水中 | ASTMD471 | 0.0 | % | |
| 23.0°C,168hr,inSodiumHydroxide,50% | ISO1817 | 0.0 | % | |
| 23.0°C,168hr,inSulfuricAcid,98% | ISO1817 | 0.0 | % | |
| 23.0°C,168hr,inSodiumChloride,15% | ISO1817 | 0.0 | % | |
| 23.0°C,168hr,inIRM903Oil | ISO1817 | 47 | % |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tear strength - transverse flow rate 2 | 23°C | ASTMD624 | 32.0 | kN/m |
| CompressionSet5 | 70°C,22hr | ISO815 | 29 | % |
| TearStrength-AcrossFlow3 | 23°C | ISO34-1 | 32 | kN/m |
| Compression permanent deformation 4 | 70°C,22hr | ASTMD395B | 29 | % |
| Tensile stress transverse flow rate | 100%Strain,23°C | ASTMD412 | 2.20 | Mpa |
| 100%Strain,23°C | ISO37 | 2.20 | Mpa | |
| Tensile strength - transverse flow rate | Break,23°C | ASTMD412 | 5.90 | Mpa |
| Tensile strength TD | Break,23°C | ISO37 | 5.90 | Mpa |
| Elongation rate - lateral flow rate | Break,23°C | ASTMD412 | 520 | % |
| Break,23°C | ISO37 | 520 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore A,15sec,23°C | ISO868 | 64 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.1mm | UL94 | HB | |
| 1.6mm | UL94 | HB | ||
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.